Abstract:Since the synthesis of non-oxidized ceramic and alloy powders requires both high temperature and oxygen insulation conditions, here we demonstrate a cost-efficient molten salt sealing/shielded synthesis method with dynamic gas tightness. Compared to conventional synthesis method, it can prevent the loss of reaction materials at high temperature, cut off the connection between reacting material and outside air, and does not require longtime ball milling mixing treatment or provision of applied pressing before or during heating. Only low-cost salts (e.g., NaCl, KCl), a few minutes of raw material mixing, and regular heating molds are required to obtain highpurity (>96 wt%), micron-sized Ti3AlC2 and Ti3SiC2 powders with narrow size distribution, which significantly decreased the complexity and production costs in the synthesis process. The effect of temperature and raw material content on the products were investigated. The mechanism of diffusion reaction between reactants in molten salt environment was analyzed. The new method developed here was also applicable to Ti2AlC, V2AlC and Cr2AlC MAX phases, as well as provided new ideas for the preparation of other MXenes precursors with certain stoichiometric ratios, air-sensitive materials and nanopowders.

Synthesis of Nano Sized Cr2AlC Powders by Molten Salt Method

In-situ Synthesis of Nanocrystalline TiC Powders, Nanorods, and Nanosheets in Molten Salt by Disproportionation Reaction of Ti(II) Species

Ternary-layered Cr2AlB2 synthesized from Cr, Al, and B powders by a molten salt-assisted method

The synthesis of high purity Ti3AlC2 MAX phase via molten salt method

Molten salt synthesis of orthorhombic CrB and Cr2AlB2 ceramics

Synthesis and characterization of submicro-sized V2AlC ceramics by a two-step modified molten salt method

Efficient synthesis of Ti3AlC2 powders with high purity by microwave-assisted molten salt method

In situ synthesis of Al2O3–SiC powders via molten-salt-assisted aluminum/carbothermal reduction method

A novel simple method to stably synthesize Ti3AlC2 powder with high purity

Synthesis of Nano-Crystalline CeO_2 Powders by DepositionMolten Salt Method

Observation on the Interface of Α-Al2o3/cr2o3: Prepared by Oxidation of Al45Cr7

Synthesis Of Nio Nano-Crystal Powders By Molten Salt Method

Facile synthesis of hollow Ti3AlC2 microrods in molten salts via Kirkendall effect

Synthesis of Stoichiometric Titanium Carbide by a Combination of Carbothermal Reduction and Molten Salt Method and Its Characterization

A New Sight on The Influence of Molten Salt in The Preparation of (Ta, Nb, Ti) C Nano‐Powder

Molten Salt Dynamic Sealing Synthesis of MAX Phases (ti3alc2, Ti3SiC2 Et Al.) Powder in Air

A possible mechanism on synthesis of Ti3AlC2

MS3, physical properties, and formation mechanism of TiV1/3Cr1/3Nb1/3AlC powders: Experimental and first-principles investigation

A New Method for Preparing Titanium Aluminium Alloy Powder

Synthesis of Ti2AlC in KBr Melt: Effect of Temperature and Component Ratio

<i>In Situ</i>Reaction Synthesis and Mechanical Properties of V<sub>2</sub>AlC