Abstract:In this paper, TiC/Al 3 Ti/Al 2 O 3 composite nanoparticles were prepared using Ti, Al, and graphite powders, in a NaCl-KCl molten salt medium. The prepared powders were characterised by X-ray diffraction (XRD), scanning electron microscopy and energy dispersive spectroscopy (SEM-EDS), and X-ray photoelectron spectroscopy (XPS). The results showed that the one-step method could only directly generate the AlTi 2 C phase, but could not generate the TiC/Al 3 Ti/Al 2 O 3 phase. In the two-step method, the Al, Al 3 Ti, Al 2 Ti, and AlTi phases were used as precursors, and then the graphite powder was added. After sintering at 1000°C for 3 h, the TiC/Al 3 Ti/Al 2 O 3 composite nano-powder was successfully prepared, which can be used as the reinforcement of Al-based composites. During the synthesis process of the TiC/Al 3 Ti/Al 2 O 3 composite nano-powder, the intermediate AlTi 2 C phase was generated first, and the exposed [Ti] in the AlTi 2 C phase adsorbed C to generate the TiC phase. The formation of the TiC phase promoted the decomposition of the AlTi 2 C phase, resulting in the formation of the Al 3 Ti phase. Finally, the residual Al phase in the molten salt was oxidised to the Al 2 O 3 phase during the washing process. Dans cet article, on a préparé des nanoparticules composites de TiC/Al 3 Ti/Al 2 O 3 en utilisant des poudres de Ti, Al et de graphite, dans un milieu de sel fondu de NaCl-KCl. On a caractérisé les poudres préparées par diffraction des rayons x (DRX), microscopie électronique à balayage et spectroscopie à dispersion d'énergie (MEB-EDS) et spectroscopie de photoélectrons X (XPS). Les résultats ont montré que la méthode en une étape ne pouvait engendrer directement que la phase AlTi 2 C, mais ne pouvait pas engendrer la phase TiC/Al 3 Ti/Al 2 O 3 . Dans la méthode en deux étapes, on a utilisé les phases Al, Al 3 Ti, Al 2 Ti et AlTi comme précurseurs, et ensuite, on a ajouté la poudre de graphite. Après frittage à 1000°C pendant 3 h, on a préparé avec succès la nano-poudre composite TiC/Al 3 Ti/Al 2 O 3 , qui peut être utilisée comme le renforcement de composites à base d'Al. Pendant le procédé de synthèse de la nano-poudre composite TiC/Al 3 Ti/Al 2 O 3 , la phase intermédiaire AlTi 2 C a été engendrée en premier, et le [Ti] exposé dans la phase AlTi 2 C a adsorbé C pour engendrer la phase TiC. La formation de la phase TiC a favorisé la décomposition de la phase AlTi 2 C, amenant la formation de la phase Al 3 Ti. Finalement, la phase Al résiduelle dans le sel fondu a été oxydée en phase Al 2 O 3 pendant le procédé de lavage.

Facile synthesis of hollow Ti3AlC2 microrods in molten salts via Kirkendall effect

In-situ Synthesis of Nanocrystalline TiC Powders, Nanorods, and Nanosheets in Molten Salt by Disproportionation Reaction of Ti(II) Species

Facile Electrosynthesis of Ti3AlC2 and Its Derived Porous Carbon in Molten Salt

The synthesis of high purity Ti3AlC2 MAX phase via molten salt method

Lewis Acid Molten Salt Etched Porous Lamellar Ti2AlC Powders for Enhanced Microwave Absorption

Sacrificial template synthesis of (V0.8Ti0.1Cr0.1)2AlC and carbon fiber@(V0.8Ti0.1Cr0.1)2AlC microrods for efficient microwave absorption

Molten salt synthesis of titanium carbide using different carbon sources as templates

Efficient synthesis of Ti3AlC2 powders with high purity by microwave-assisted molten salt method

In Situ Synthesis of Ti2AlC–Al2O3/TiAl Composite by Vacuum Sintering Mechanically Alloyed TiAl Powder Coated with CNTs

V2(Al1−xGax)C microrods synthesized through molten-salt show efficient microwave absorption capability

Synthesis of Nano Sized Cr2AlC Powders by Molten Salt Method

Synthesis and characterization of submicro-sized V2AlC ceramics by a two-step modified molten salt method

Composition and structure of Ti–Al alloy powders formed by electrochemical co-deposition in KCl–LiCl–MgCl2–TiCl3–AlCl3 molten salt

Controlled Synthesis of TiC Nanoparticles Using Solid Oxide Membrane Technology in Molten CaCl2

A possible mechanism on synthesis of Ti3AlC2

A novel simple method to stably synthesize Ti3AlC2 powder with high purity

Formation mechanism of Ti3AlC2 in TiO2–Al–C/TiC systems at high temperatures

Green preparation and synthesis mechanism of TiC/Al3Ti/Al2O3 composite nanoparticles

Molten Salt Dynamic Sealing Synthesis of MAX Phases (ti3alc2, Ti3SiC2 Et Al.) Powder in Air

Formation of TiC/Ti 2 AlC and Α 2 +γ in In-Situ TiAl Composites with Different Solidification Paths

Synthesis of Submicrometer-Sized TiC Particles in Aluminum Melt at Low Melting Temperature