Abstract:In this study, K 2 TiF 6 and C powder (Ti:C atomic ratio 1:1) are introduced into Al-Si-Fe alloy by contact reaction method. The focus of this study is to investigate the reaction and precipitation behavior of Ti source in the alloy melt, and the effect of reaction products on the microstructure and properties of Al-Si-Fe alloy. The results show that the reaction products formed between Ti and the matrix alloy can destroy the acicular β-Fe phase in the original alloy. The transformation results in the a morphological change of the alloy from needle-like structure to Chinese script and fishbone-like structure, which effectively improves the mechanical properties of the alloy. The DSC analysis results indicate that Al-Si- Fe powder, K 2 TiF 6 powder, and C powder undergo significant exothermic reactions at around 950 °C, corresponding to the formation of TiC. Further microscopic morphology observations support the inference that TiC powders formed in this temperature range. Firstly, the synthesis of the matrix takes place at 580 °C. K 2 TiF 6 mixed with alloy powder shows an obvious exothermic peak at 660 °C, corresponding to the formation of the second phase Al 3 Ti by wetting and chemical reaction. However, it is worth noting that the reaction intermediate product(Al 4 C 3 phase) consumes three times as much Al 3 Ti as itself. As a result, the exothermic peak generated by Al 3 Ti disappears. Lastly, a long-term exothermic reaction that takes place above 850 °C lead to the gradual replacement of the Al 3 Ti phase by TiC particles. The mechanical properties test indicates that the needle-shaped Al 3 Ti to some extent deteriorates the alloy's properties. But the final product (TiC) can offset the deteriorating effect of Al 3 Ti and restore the alloy's property.

A possible mechanism on synthesis of Ti3AlC2

Preparation of Ti3AlC2 and Ti2AlC by self-propagating high-temperature synthesis and study on the reaction mechanism

Formation mechanism of Ti3AlC2 in TiO2–Al–C/TiC systems at high temperatures

A novel simple method to stably synthesize Ti3AlC2 powder with high purity

Combustion synthesis of ternary carbide Ti3AlC2 in Ti–Al–C system

Effects of different Ti/C and Al contents on combustion synthesized Ti3AlC2 powders in the Ti-Al-C system

Formation Mechanisms of Ti2AlC and Ti3AlC During Solid-State Sintering Between Multilayer Graphene and TiAl Alloy Composite

Combustion synthesis ternary carbide Ti2AlC1-x

Solid–liquid Reaction Synthesis of Layered Machinable Ti3AlC2 Ceramic

Synthesis of High Purity Ti3AlC2 Bulk Material by Hot-Pressing

Synthesis and mechanical properties of Ti 3 AlC 2 by spark plasma sintering

Effects of different Al contents on combustion synthesis of Ti3AlC2 powders in the Ti-Al-C system

Kinetic Process of Combustion Synthesis of Ternary Carbide Ti<sub>3</sub>AlC<sub>2</sub>

Effect of Sn and Si on the Synthesis of Ti<sub>3</sub>Al(Sn/Si)C<sub>2</sub> by Self-Propagating High-Temperature Sintering

PREPARATION OF Ti3AlC2 AND Ti2AlC BY SELF-PROPAGATING HIGH-TEMPERATURE SYNTHESIS AND STUDY ON MECHANISM OF THE REACTION

Reaction mechanism of Ti3SiC2 formed on the diamond

Preparation of Ti 3 AlC 2 and Ti 2 AlC by self-propagating high-temperature synthesis

Effects of TiAl3 addition on combustion synthesis of Ti3AlC

Reaction Mechanism of Ti<SUB>3</SUB>SiC<SUB>2</SUB> Formed on the Diamond

Effects of TiAl additions on combustion synthesis of Ti3AlC2 powders

Thermodynamic Investigation on K2TiF6 and C Powder to Prepared in-situ TiCp in Molten Al-Si-Fe Alloy