Abstract:TiAl intermetallic compounds, as a new kind of high-performance light-weight structural material, are widely applied in many fields. Titanium carbide (TiC) as the reinforcing phase could improve the mechanical properties, wear resistance, and heat-resistance stability of TiAl intermetallic compounds. Ti(Al, C) mixture powders were deposited by cold spraying at gas temperature of 250 °C, 450 °C, and 550 °C. Then, Ti(Al, C) coatings were annealed at temperatures of 650 °C for different times and following holding at 1100 °C for 3 h. The microstructure, microhardness, fracture toughness, and abrasive wear of Ti-Al composite coatings were investigated. The research results were that the particle size of mixture powders decreased as the ball milling time prolonging. Ti(Al) solid solution appeared in the mixture powders as the milling time increased to 30 h. The average porosity of the coating sprayed at 550 °C was the lowest (0.85%). The as-sprayed coatings exhibited the same phase compositions with the mixture powders. The coating sprayed at gas temperature of 550 °C has the highest microhardness and the lowest weight loss. Ti-Al intermetallic was in-situ synthesized after annealing at 650 °C. The average porosity of the annealed coating (sprayed at 450 °C) was the lowest. The content of Ti-Al intermetallic compounds of the annealed coating sprayed at 450 °C is the highest. The X-ray diffraction (XRD) analysis results are consistent with the EDS analysis of the annealed coatings after annealing at 650 °C. Ti-Al intermetallic compounds were almost completely formed in the three kinds of the coatings after annealing at 650 °C for 20 h and following holding at 1100 °C for 3 h. TiAl and TiAl3 intermetallic phases were in-situ synthesized in the coatings based on the energy dispersive spectroscopy (EDS) and XRD analysis. TiC was also in situ synthesized in the coatings as the annealing temperature increased to 1100 °C. The annealed coating (sprayed at 450 °C) has the highest microhardness, fracture toughness, and wear resistance properties after annealing at 1100 °C for 3 h.

Preparation of Ti3AlC2 and Ti2AlC by self-propagating high-temperature synthesis and study on the reaction mechanism

PREPARATION OF Ti3AlC2 AND Ti2AlC BY SELF-PROPAGATING HIGH-TEMPERATURE SYNTHESIS AND STUDY ON MECHANISM OF THE REACTION

Preparation of Ti 3 AlC 2 and Ti 2 AlC by self-propagating high-temperature synthesis

Effect of Sn and Si on the Synthesis of Ti<sub>3</sub>Al(Sn/Si)C<sub>2</sub> by Self-Propagating High-Temperature Sintering

Self-Propagating High-Temperature Synthesis in a Ti−Al−C Powder System Using Different Carbon Precursors

Preparation of Al–TiC Composites by Self-Propagating High-Temperature Synthesis

A possible mechanism on synthesis of Ti3AlC2

A novel simple method to stably synthesize Ti3AlC2 powder with high purity

Formation mechanism of Ti3AlC2 in TiO2–Al–C/TiC systems at high temperatures

In Situ Synthesis of Al–TiC in Aluminum Melt

Kinetics and numerical simulation of self-propagating high-temperature synthesis in Ti–Cr–Al–C systems

Synthesis Of High-Purity Powder Ti3alc2 Materials By Pressureless Sintering

Synthesis of high pure Ti3AlC2 and Ti2AlC powders from TiH2 powders as Ti source by tube furnace

Effects of different Ti/C and Al contents on combustion synthesized Ti3AlC2 powders in the Ti-Al-C system

Effects of different Al contents on combustion synthesis of Ti3AlC2 powders in the Ti-Al-C system

Synthesis of High Purity Ti3AlC2 Bulk Material by Hot-Pressing

Combustion synthesis of ternary carbide Ti3AlC2 in Ti–Al–C system

Mathematical and experimental investigation of the self-propagating high-temperature synthesis (SHS) of TiAl3 and Ni3Al intermetallic compounds

Effects of TiAl3 addition on combustion synthesis of Ti3AlC

A novel route for preparing Ti3AlC2 ceramics

Microstructure, Microhardness, Fracture Toughness, and Abrasive Wear of In-Situ Synthesized TiC/Ti-Al Composite Coatings by Cold Spraying Combined with Heat Treatment