Synthesis Of High-Purity Powder Ti3alc2 Materials By Pressureless Sintering

Cq Peng,Ca Wang,Y Huang

DOI: https://doi.org/10.3321/j.issn:1002-185X.2005.z1.145

2005-01-01

Rare Metal Materials and Engineering

Abstract:Ti3AlC2 powder materials with high-purity was prepared by pressureless sintering. The starting materials were TiC, Ti and Al powders, with a molar ratio of TiC : Ti : Al = 2 : 1.2 : 1. The effect of different sintering temperature from 1200 degrees C similar to 1500 degrees C, holding-time from 15min to 60 min on the microstructure was investigated. The results showed that high-pure Ti3AlC2 powders could be prepared by sintering the starting materials at 1300 degrees C similar to 1400 degrees C, held for 15min, and the purity of Ti3AlC2 could reach 96.76%. In addition, in the sample sintered at 1500 degrees C, the particle sizes were so big that obvious preferred orientation appeared in the XRD pattern of the powder, and the intensity of {002) peak of Ti3AlC2 was exceptionally high.