Abstract:A ternary carbide phase, namely Ti3AlC2, was successfully synthesized by hot pressing (HP) and spark plasma sintering (SPS), respectively, from the starting materials of Ti, Al4C3 and activated carbon. The soaking temperature of HP process was 1400°C and the soaking time varied from 5 to 120 min. The soaking temperature of SPS process was 1300°C and the soaking time varied from 1 to 7 min. Based on the results of X-ray diffractometer (XRD) and scanning electron microscopy (SEM), a possible mechanism was presented: firstly, at a certain sintering temperature, plenty of Ti6C octahedra are formed. Thereafter, two different intermediate products are obtained from the Ti6C octahedra depending on different soaking temperatures. One intermediate product is Ti2AlC obtained by linking every layer of Ti6C octahedra together by an aluminum plane. The other is TiC obtained by linking the Ti6C octahedra together directly. Finally, the intermediate products transform to Ti3AlC2 as the soaking time is extended. Ti2AlC loses half of its aluminum layers and then transforms to Ti3AlC2. Ti6C octahedra in TiC crystals are separated by aluminum planes and then TiC transforms to Ti3AlC2.

PREPARATION OF Ti3AlC2 AND Ti2AlC BY SELF-PROPAGATING HIGH-TEMPERATURE SYNTHESIS AND STUDY ON MECHANISM OF THE REACTION

Preparation of Ti3AlC2 and Ti2AlC by self-propagating high-temperature synthesis and study on the reaction mechanism

Preparation of Ti 3 AlC 2 and Ti 2 AlC by self-propagating high-temperature synthesis

Effect of Sn and Si on the Synthesis of Ti<sub>3</sub>Al(Sn/Si)C<sub>2</sub> by Self-Propagating High-Temperature Sintering

Preparation of Al–TiC Composites by Self-Propagating High-Temperature Synthesis

Self-Propagating High-Temperature Synthesis in a Ti−Al−C Powder System Using Different Carbon Precursors

Combustion Synthesis and Thermal Stability of Ti3AlC2

A novel simple method to stably synthesize Ti3AlC2 powder with high purity

In situ fabrication of TiC particulates locally reinforced aluminum matrix composites by self-propagating reaction during casting

Synthesis Mechanism of TiC Particles in Preparation of AlTiC Intermediate Alloys

Fabrication of Ti3AlC2 by Self-Propagating High-Temperature Synthesis and Its Friction and Wear Behavior

Formation mechanism of Ti3AlC2 in TiO2–Al–C/TiC systems at high temperatures

A possible mechanism on synthesis of Ti3AlC2

Study of formation behavior of TiC ceramic obtained by self-propagating high-temperature synthesis from Al–Ti–C elemental powders

A synthesis method of Ti3AlC2 ceramic

Microstructural Evolution During Self-Propagating High Temperature Synthesis of Ti2AlC Machinable Ceramics

Joining of TiAl Intermetallic by Self-Propagating High-Temperature Synthesis

Rapid Synthesis of Bulk Ti2alc by Self-Propagating High Temperature Combustion Synthesis with A Pseudo-Hot Isostatic Pressing Process

Reactive Synthesis of Polycrystalline Ti3AlC2 and Its Sintering Behavior

High Temperature Oxidation Behavior of Ti_3AlC_2 Ceramics Prepared by SHS/PHIP

Mathematical and experimental investigation of the self-propagating high-temperature synthesis (SHS) of TiAl3 and Ni3Al intermetallic compounds