Abstract:In this paper, TiC/Al 3 Ti/Al 2 O 3 composite nanoparticles were prepared using Ti, Al, and graphite powders, in a NaCl-KCl molten salt medium. The prepared powders were characterised by X-ray diffraction (XRD), scanning electron microscopy and energy dispersive spectroscopy (SEM-EDS), and X-ray photoelectron spectroscopy (XPS). The results showed that the one-step method could only directly generate the AlTi 2 C phase, but could not generate the TiC/Al 3 Ti/Al 2 O 3 phase. In the two-step method, the Al, Al 3 Ti, Al 2 Ti, and AlTi phases were used as precursors, and then the graphite powder was added. After sintering at 1000°C for 3 h, the TiC/Al 3 Ti/Al 2 O 3 composite nano-powder was successfully prepared, which can be used as the reinforcement of Al-based composites. During the synthesis process of the TiC/Al 3 Ti/Al 2 O 3 composite nano-powder, the intermediate AlTi 2 C phase was generated first, and the exposed [Ti] in the AlTi 2 C phase adsorbed C to generate the TiC phase. The formation of the TiC phase promoted the decomposition of the AlTi 2 C phase, resulting in the formation of the Al 3 Ti phase. Finally, the residual Al phase in the molten salt was oxidised to the Al 2 O 3 phase during the washing process. Dans cet article, on a préparé des nanoparticules composites de TiC/Al 3 Ti/Al 2 O 3 en utilisant des poudres de Ti, Al et de graphite, dans un milieu de sel fondu de NaCl-KCl. On a caractérisé les poudres préparées par diffraction des rayons x (DRX), microscopie électronique à balayage et spectroscopie à dispersion d'énergie (MEB-EDS) et spectroscopie de photoélectrons X (XPS). Les résultats ont montré que la méthode en une étape ne pouvait engendrer directement que la phase AlTi 2 C, mais ne pouvait pas engendrer la phase TiC/Al 3 Ti/Al 2 O 3 . Dans la méthode en deux étapes, on a utilisé les phases Al, Al 3 Ti, Al 2 Ti et AlTi comme précurseurs, et ensuite, on a ajouté la poudre de graphite. Après frittage à 1000°C pendant 3 h, on a préparé avec succès la nano-poudre composite TiC/Al 3 Ti/Al 2 O 3 , qui peut être utilisée comme le renforcement de composites à base d'Al. Pendant le procédé de synthèse de la nano-poudre composite TiC/Al 3 Ti/Al 2 O 3 , la phase intermédiaire AlTi 2 C a été engendrée en premier, et le [Ti] exposé dans la phase AlTi 2 C a adsorbé C pour engendrer la phase TiC. La formation de la phase TiC a favorisé la décomposition de la phase AlTi 2 C, amenant la formation de la phase Al 3 Ti. Finalement, la phase Al résiduelle dans le sel fondu a été oxydée en phase Al 2 O 3 pendant le procédé de lavage.

The synthesis of high purity Ti3AlC2 MAX phase via molten salt method

In-situ Synthesis of Nanocrystalline TiC Powders, Nanorods, and Nanosheets in Molten Salt by Disproportionation Reaction of Ti(II) Species

Efficient synthesis of Ti3AlC2 powders with high purity by microwave-assisted molten salt method

Facile Electrosynthesis of Ti3AlC2 and Its Derived Porous Carbon in Molten Salt

Synthesis of Nano Sized Cr2AlC Powders by Molten Salt Method

Molten Salt Dynamic Sealing Synthesis of MAX Phases (ti3alc2, Ti3SiC2 Et Al.) Powder in Air

Molten salt-shielded solid-state synthesis (MS5) reaction-driven >99% pure Ti3AlC2 MAX phase: effect of MAX phase purity on the interlayer separation of MXenes and Na-ion storage

A novel simple method to stably synthesize Ti3AlC2 powder with high purity

Synthesis of Ti2AlC in KBr Melt: Effect of Temperature and Component Ratio

Rapid synthesis of high‐yield Ti3AlC2 MAX phase powders from TiC0.67 and Al with induction heating assistance

Pressureless manufacturing of high purity Ti3AlC2 MAX phase material: Synthesis and characterisation

Facile synthesis of hollow Ti3AlC2 microrods in molten salts via Kirkendall effect

Synthesis of MAX Phases in the Ti2AlC–V2AlC System as Precursors of Heterometallic MXenes Ti2 – xVxC

Preparation and performance of MAX phase Ti3AlC2 by in-situ reaction of Ti-Al-C system

Electrolytic synthesis of TiC/SiC nanocomposites from high titanium slag in molten salt

Synthesis and characterization of submicro-sized V2AlC ceramics by a two-step modified molten salt method

Topotactic transition of Ti4AlN3 MAX phase in Lewis acid molten salt

Synthesis of glucose‐derived MAX phases and investigation on the phase evolution behavior

Synthesis of low-cost Ti3AlC2-Ti2AlC dual MAX phase with high-electrical conductivity using economical raw materials and novel compositions

Synthesis and Reaction Path of Ti‐Al‐C MAX Phase by Reaction with Ti‐Al Intermetallic Compounds and TiC

Green preparation and synthesis mechanism of TiC/Al3Ti/Al2O3 composite nanoparticles