Abstract:MXenes are a large family of two-dimensional materials that have attracted attention across many fields due to their desirable optoelectronic, biological, mechanical and chemical properties. There currently exist many synthesis procedures that lead to differences in flake size, defects and surface chemistry, which in turn affect their properties. Herein, we describe the steps to synthesize Ti 3 C 2 T x —the most important and widely used MXene, from a Ti 3 AlC 2 MAX phase precursor. The procedure contains three main sections: synthesis of Ti 3 AlC 2 MAX, wet chemical etching of the MAX in hydrofluoric acid/HCl solution to yield multilayer Ti 3 C 2 T x and its delamination into single-layer flakes. Three delamination options are described; these use LiCl, tertiary amines (tetramethyl ammonium hydroxide/ tetrabutyl ammonium hydroxide) and dimethylsulfoxide respectively. These procedures can be adapted for the synthesis of MXenes beyond Ti 3 C 2 T x . The MAX phase synthesis takes about 1 week, with the etching and delamination each requiring 2 d. This protocol requires users to have experience working with hydrofluoric acid, and it is recommended that users have experience with wet chemistry and centrifugation; characterization techniques such as X-ray diffraction and particle size analysis are also essential for the success of the protocol. While alternative synthesis methods, such as minimally intensive layer delamination, are desirable for certain MXenes (such as Ti 2 CT x ) or specific applications, this protocol aims to standardize the more commonly used hydrofluoric acid/HCl etching method, which produces Ti 3 C 2 T x with minimal concentration of defects and the highest conductivity and serves as a guideline for those working with MXenes for the first time.

Synthesis of glucose‐derived MAX phases and investigation on the phase evolution behavior

Synthesis of MAX Phase Nanofibers and Nanoflakes and the Resulting MXenes

Porous Ti3AlC2 MAX phase enables efficient synthesis of Ti3C2Tx MXene

Facile Electrosynthesis of Ti3AlC2 and Its Derived Porous Carbon in Molten Salt

Molten salt-shielded solid-state synthesis (MS5) reaction-driven >99% pure Ti3AlC2 MAX phase: effect of MAX phase purity on the interlayer separation of MXenes and Na-ion storage

Maximizing Potential Applications of MAX Phases: Sustainable Synthesis of Multielement Ti3AlC2

The synthesis of high purity Ti3AlC2 MAX phase via molten salt method

Large-scale Conformal Synthesis of One-Dimensional MAX Phases

Synthesis of MAX Phases in the Ti2AlC–V2AlC System as Precursors of Heterometallic MXenes Ti2 – xVxC

High‐Entropy Carbonitride MAX Phases and Their Derivative MXenes

First-principles Study for Discovery of Novel Synthesizable 2D High-entropy Transition Metal Carbides (MXenes)

Comprehensive synthesis of Ti 3 C 2 T x from MAX phase to MXene

In Situ Synthesis of MXene with Tunable Morphology by Electrochemical Etching of MAX Phase Prepared in Molten Salt

Operando Exploring and Modulating Phase Evolution Chemistry from MAX to MXenes in Molten Salt Synthesis

Solvent-Free One-Step Green Synthesis of Mxenes by “Gas-Phase Selective Etching”

Synthesis and characterization of chromium aluminum carbide MAX phases (CrxAlCx-1) for potential biomedical applications

Molten Salt Dynamic Sealing Synthesis of MAX Phases (ti3alc2, Ti3SiC2 Et Al.) Powder in Air

Novel Synthesis of Red Phosphorus Nanodot/Ti3C2Tx MXenes from Low-Cost Ti3SiC2 MAX Phases for Superior Lithium- and Sodium-Ion Batteries

Structural, Morphological and Elemental Analysis of Selectively Etched and Exfoliated Ti3AlC2 MAX Phase

Molten salt synthesis of a nanolaminated Sc2SnC MAX Phase

General and Fast Gas–Solid Synthesis of Functional MXenes and Derivatives on the Scale of Tens of Grams