Abstract:The caking and adhesion of intermediate product on reactor surfaces during TiO2 production via the NaOH molten salt method are a serious problem. The consolidation of intermediate product can lead to low heat transfer efficiency and low titanium fractional conversion. Furthermore, frequent cleaning is generally required. An anti-caking method that can be applied during low-grade titanium slag decomposition in the NaOH system was studied. The method, which involves the two-step reaction of low-grade titanium slag with molten NaOH without the introduction of additives, can significantly reduce the extent of caking. The NaOH and low-grade titanium slag mixture was first reacted at 350°C for 60min. The temperature was then increased to 550°C in 40min. Finally, the mixture was reacted at 550°C for 75min. The effects of the reaction temperatures, NaOH-to-slag mass ratio and the reaction time on the titanium extraction were investigated. The Brunauer–Emmett–Teller (BET) surface area and apparent density were used to characterize the extent of caking. In the low grade titanium slag, silicate phase prior to pseudobrookite phase reacts with molten NaOH at 350°C in the process of two-step molten reaction and formed sodium silicate. Microstructural and Fourier transform infrared (FT-IR) absorption results show that the firstly formed sodium silicate did not diffuse into the entire reaction system and powder-shaped intermediate product was formed. Approximately 97% of titanium in the titanium slag could be extracted under the optimal reaction conditions. In addition, the content of TiO2 obtained in the product reached 99.3%.

Electrolytic synthesis of TiC/SiC nanocomposites from high titanium slag in molten salt

Preparation of TiC/SiC composites from Ti-enriched slag by an electrochemical process in molten salts

In-situ Synthesis of Nanocrystalline TiC Powders, Nanorods, and Nanosheets in Molten Salt by Disproportionation Reaction of Ti(II) Species

Electrosynthesis of Titanium from High-Titanium Slag with Short-Process in Molten CaCl2

Carbochlorination of Low-Grade Titanium Slag to Titanium Tetrachloride in Molten Salt

Synthesis of Stoichiometric Titanium Carbide by a Combination of Carbothermal Reduction and Molten Salt Method and Its Characterization

Direct selective extraction of titanium silicide Ti5Si3 from multi-component Ti-bearing compounds in molten salt by an electrochemical process

Molten salt synthesis of titanium carbide using different carbon sources as templates

Direct Electrosynthesis of Fe-TiC Composite from Natural Ilmenite in Molten Calcium Chloride

Electrolytic preparation of porous TiSi2/Si nanocomposites and the electrochemical performances as lithium-ion battery anode

Anti-caking in the production of titanium dioxide using low-grade titanium slag via the NaOH molten salt method

Preparation of Titanium by Electro-deoxidation of CaTiO3 in a Molten CaCl2-NaCl Salt

The synthesis of high purity Ti3AlC2 MAX phase via molten salt method

Preparation of rutile titanium dioxide pigment from low-grade titanium slag pretreated by the NaOH molten salt method

Thermodynamic design of electroslag remelting slag for high titanium and low aluminium stainless steel based on IMCT

Electrochemical extraction of Ti5Si3 silicide from multicomponent Ti/Si-containing metal oxide compounds in molten salt

Manipulation Of Phase And Microstructure At Nanoscale For Sic In Molten Salt Synthesis

Preparation of high-purity TiSi2 and eutectic Si–Ti alloy by separation of Si–Ti alloy for clean utilization of Ti-bearing blast furnace slag

Titanium metallization of Si3N4 ceramics by molten salt reaction: Mechanism and interfacial structure