Abstract:An innovative process for preparing silicon carbide (SiC) from acid leaching residue of ferronickel slag through a carbon–thermal reduction process was proposed in this study. The results indicate that the acid leaching residue is an ideal silicon source for SiC preparation according to its high amorphous silica content of 84.20% and fine particle size of d50 = 29.16 μm. Compared with carbon black, activated carbon, and graphite, coke is the more appropriate carbon source for SiC preparation. A micron-size SiC powder with grade of 88.90% and an average particle size (d50) of 44.68 μm can be obtained under the following conditions: the mass ratio of coke to leaching residue as 1.2:1, in an air atmosphere, reducing at 1600 °C for 3 h, following by decarbonizing at 700 °C for 4 h. The XRD, SEM and FTIR analyses show that the prepared powder is 3C-SiC and belongs to the β-SiC crystal type. Based on thermodynamic analysis and micromorphology observation, it can be concluded that with amorphous silica as the silicon source, the carbon–thermal synthesis of SiC powder follows both the solid–solid reaction mechanism and the gas–solid mechanism. The SiC created through solid–solid reaction is primarily nucleated in situ on amorphous SiO2, with a size close to that of the original acid-leaching slag, while the SiC generated according to the gas–solid mechanism mainly nucleates heterogeneously on the surface of carbon particles, resulting in a smaller particle size and mostly adhering to the surface of solid–solid nucleated SiC particles. This study provides a feasible method for the effective utilization of amorphous silica, which is also significant for the efficient consumption of the vast acid leaching residue.

Preparation of TiC/SiC composites from Ti-enriched slag by an electrochemical process in molten salts

Electrolytic synthesis of TiC/SiC nanocomposites from high titanium slag in molten salt

Electrosynthesis of Titanium from High-Titanium Slag with Short-Process in Molten CaCl2

Preparation of Titanium by Electro-deoxidation of CaTiO3 in a Molten CaCl2-NaCl Salt

Direct selective extraction of titanium silicide Ti5Si3 from multi-component Ti-bearing compounds in molten salt by an electrochemical process

In-situ Synthesis of Nanocrystalline TiC Powders, Nanorods, and Nanosheets in Molten Salt by Disproportionation Reaction of Ti(II) Species

Direct Electrosynthesis of Fe-TiC Composite from Natural Ilmenite in Molten Calcium Chloride

Electrochemical extraction of Ti5Si3 silicide from multicomponent Ti/Si-containing metal oxide compounds in molten salt

Carbochlorination of Low-Grade Titanium Slag to Titanium Tetrachloride in Molten Salt

Electrochemical extraction of titanium from carbon-doped titanium dioxide precursors by electrolysis in chloride molten salt

Preparation of high-purity TiSi2 and eutectic Si–Ti alloy by separation of Si–Ti alloy for clean utilization of Ti-bearing blast furnace slag

Corrosion behaviors of Ti3SiC2/Cu composites in molten salts

Preparation of rutile titanium dioxide pigment from low-grade titanium slag pretreated by the NaOH molten salt method

Oxidation Kinetics and Mechanism of TiC with Simulated Blast‐Furnace Gases

Synthesis of micro-FeTi powders by direct electrochemical reduction of ilmenite in CaCl2-NaCl molten salt

Preparation of Silicon Carbide Powder from Amorphous Silica and Investigation of Synthesis Mechanism

A novel process for preparation of titanium dioxide from Ti-bearing electric furnace slag: NH4HF2-HF leaching and hydrolyzing process

Thermodynamic design of electroslag remelting slag for high titanium and low aluminium stainless steel based on IMCT

Sintering properties and microstructure of Al2O3-TiO2-CaO composite materials based on ferrotitanium slag