Abstract:<p class="a-plus-plus">The high-temperature interactions between vanadium-titanium magnetite carbon composite hot briquettes (VTM-CCBs) and pellets were systematically investigated under simulated blast furnace conditions with respect to the reduction behavior, softening–melting–dripping characteristics, gas permeability, and Ti(C, N) precipitation mechanisms. The results showed that VTM-CCB charging can promote the reduction of the pellet in the packed bed and decrease the compressive strength of the pellet after reduction. The compressive strength of the VTM-CCB after reduction decreased with increasing temperature when the FC/O ratio (the ratio of the fixed carbon mol(C) in coal to the reducible oxygen mol(O) in iron oxides) was higher than 1.0. With an FC/O ratio lower than 1.0, the compressive strength of the VTM-CCB initially decreased and then increased. The FC/O ratio has a significant influence on the softening–melting interaction mechanism between the VTM-CCB and the pellet. With an FC/O ratio of 0.8, the bonding layer at the interface between the pellet and the VTM-CCB (consisting of molten fayalitic slag) can promote the softening process, thereby decreasing the softening start and end temperatures. By increasing the FC/O ratio to 1.4, a dense metallic iron shell with relatively high strength formed at the interface and restricted the collapse of the packed bed, thereby increasing the softening start and end temperatures and ensuring the transport of the reduction gas through the packed bed. The melting point of the primary slag phase increased with increasing FC/O ratio due to a decrease in the FeO content, which resulted in an increase in the melting start temperature from 1273 °C to 1294 °C (1546 K to 1567 K). The gas permeability in the cohesive zone increased with an increasing FC/O ratio of the VTM-CCB due to a combination of the skeletal role performed by the residual VTM-CCB and the decrease in the liquid slag proportion. In addition, as the FC/O ratio increased to 1.4, unconsumed carbon promoted the precipitation of Ti(C, N) at the slag–carbon and slag–metal interfaces, which resulted in a substantial increase in the dripping temperature and deterioration of the dripping behavior of the packed bed. Therefore, to suppress the precipitation of Ti(C, N) and improve the dripping behavior of the packed bed, the FC/O ratio of the charged VTM-CCB should be controlled within an appropriate range.</p>

Oxidation Kinetics and Mechanism of TiC with Simulated Blast‐Furnace Gases

Improving the Comprehensive Properties of ZrO2–C Materials with Aid of TiO2 Addition

Study on the High-temperature Properties of High-titania Slags produced with Cr-bearing Vanadia-titania Magnetite Smelting in Blast Furnace

Dissolution characteristics of TiC0.3N0.7 in low-carbon and safe blast furnace hearth

Combined Effect of SiO2 and O2 on the Crystallization Behavior of Modified Ti-Bearing Blast Furnace Slag

Mechanochemical activation of titanium slag for effective selective catalytic reduction of nitric oxide

Kinetics of Oxidation of an Al2O3–SiC–C‐Based Blast Furnace Trough Refractory in Air

Interface Wetting Behavior Between Iron and Coke During the Carbon Dissolution Process in a Blast Furnace

A thermodynamic model for predicting activity of CaO–SiO2–Al2O3–MgO–TiO2–V2O3–FeO slags during electric furnace smelting process

Co-modification and Crystalline-control of Ti-bearing Blast Furnace Slags

Mechanisms responsible for enhancing low‐temperature oxidation resistance of nonstoichiometric (Zr,Ti)C

A novel recycling approach for efficient extraction of titanium from high-titanium-bearing blast furnace slag

Effect of Cr2O3 content on viscosity and phase structure of chromium-containing high-titanium blast furnace slag

Kinetics of carbon oxidation reaction between molten iron of high carbon concentration and iron oxide containing slag.

Elucidating the role of Ti3AlC2 and Ti3SiC2 in oxidation mechanisms of MgO–C refractories

High-Temperature Interactions Between Vanadium-Titanium Magnetite Carbon Composite Hot Briquettes and Pellets Under Simulated Blast Furnace Conditions

Regulation of Ti(C,N) deposition on hot surface of refractory in blast furnace hearth

Oxidation mechanism of Ti‐Doped Fe3O4 (111): A combined DFT and AIMD study with an experimental verification

Preparation of Titanium by Electro-deoxidation of CaTiO3 in a Molten CaCl2-NaCl Salt

Influence of Basicity and TiO2 Content on the Precipitation Behavior of the Ti-bearing Blast Furnace Slags