Abstract:A systematic study on the mechano-thermic reduction of low-grade ilmenite concentrate for the production of high-grade TiO 2 powder used in the production of non-oxide ceramics for cutting tool applications has been successfully carried out. Samples were prepared via planetary ball milling and carbothermic reduction processes, and the as-reduced product was subsequently leached in order to improve the synthesized TiO 2 by removing the metallic iron in it and other minor soluble impurities dissolved in the iron. The mechano-thermic reduction was achieved by milling a representative mixture of ilmenite and carbon in a molar ratio of 1:1, followed by carbothermic reduction at 1000 °C in a laboratory high-temperature furnace for 60 min. The as-reduced product was subsequently leached at 80 °C for 6 h in a hydrochloric acid solution. It was found that there was a complete reduction of ilmenite to metallic iron and TiO 2 at 1000 °C. The results of the FESEM showed there were only two distinct regions of metallic iron (bright region) and titanium dioxide (grey region) with minor traces of unreacted carbon (dark spots), although there was clear regional demarcation between these regions. However, the iron dissolution during the acid treatment was almost 100% as there were no peaks of iron in the as-leached powder. The results of these analyses confirmed the synthesis of high-grade TiO 2 , which finds application in cutting tool applications and other areas such as in reflective pigment production.

Direct Electrosynthesis of Fe-TiC Composite from Natural Ilmenite in Molten Calcium Chloride

Scalable Synthesis of Fe3O4/C Composites with Enhanced Electrochemical Performance As Anode Materials for Lithium-Ion Batteries

Synthesis of micro-FeTi powders by direct electrochemical reduction of ilmenite in CaCl2-NaCl molten salt

Liquid‐Metal‐Assisted Synthesis of Single‐Crystalline TiC Nanocubes with Exposed {100} Facets for Enhanced Electrocatalytic Activity in the Hydrogen Evolution Reaction

Preparation of Ferrotitanium Alloy from Ilmenite by Electrochemical Reduction in Chloride Molten Salts

Preparation of Ferrotitanium from Ilmenite by Electrolysis-Assisted Calciothermic Reduction in CaCl2-NaCl Molten Salt

Direct Electro-deoxidation of Ilmenite Concentrate to Prepare FeTi Alloy in CaCl2 Molten Salt

Preparation of TiC/SiC composites from Ti-enriched slag by an electrochemical process in molten salts

In-situ Synthesis of Nanocrystalline TiC Powders, Nanorods, and Nanosheets in Molten Salt by Disproportionation Reaction of Ti(II) Species

Experimental investigation on the formation mechanism of the TiFe alloy by the molten-salt electrolytic titanium concentrate

Electrolytic synthesis of TiC/SiC nanocomposites from high titanium slag in molten salt

Mechano-thermic reduction of low-grade titanium ore for high-grade TiO2 synthesis

Combustion Synthesis of TiC–Fe Composites under the Action of an Electric Field

Reactive Products of Carbothermic Reduction of Ilmenite in Mixed Air for Iron-Based Ti(C,N) Composite

Direct selective extraction of titanium silicide Ti5Si3 from multi-component Ti-bearing compounds in molten salt by an electrochemical process

Electrosynthesis of Titanium from High-Titanium Slag with Short-Process in Molten CaCl2

Extraction of titanium from different titania precursors by the FFC Cambridge process

Synthesis and Characterization of TiC Nanofibers Obtained via a Modified Carbothermal Process

Direct Synthesis of Controllable Microstructures of Thermally Stable and Ordered Mesoporous Crystalline Titanium Oxides and Carbide/Carbon Composites

Electro-Chemical Preparation of Tio2/Cnt Electrodes with Tnb Electrolyte and Their Photoelectrocatalytic Effect

Synthesis of ordered mesoporous crystalline carbon-anatase composites with high titania contents.