Abstract:As the titanium industry rapidly develops, low-grade ilmenite resources are drawing global attention. The direct use of low-grade ilmenite can result in low production efficiency and heavy pollution. In addition, the production of high-titanium slag via electric furnace melting consumes significant energy and possesses low production efficiency. Therefore, a novel process with low energy consumption is necessary for producing ultra-grade slag (UGS) for chlorination. For low-grade ilmenite, semi-molten reduction and magnetic separation were suggested in this study. The effects of carbon content, reduction time, and Na2CO3 addition on the reduction and separation behavior were studied. The results showed that the addition of Na2CO3 favored the formation of a semi-molten state, which was more conducive for the diffusion, aggregation, and growth of the metal phase. In this regard, excess carbon was not helpful, and it weakened the growth of the metal phase. Wet grinding and magnetic separation were used for beneficiation of the reduced sample for efficiently separating the slag iron and preventing the formation of agglomerates between slag and metal. For the sample with a carbon dosage of 13 pct, Na2CO3 dosage of 8 pct, reduction temperature of 1673 K (1400 °C), and 90 minutes holding time, high-titanium slag with a TiO2 grade of 81.63 pct and iron content of 4.53 pct was produced, with the TiO2 recovery rate of 93.43 pct and the yields of 55.37 pct. High-titanium slag can be used as a high-quality raw material to produce UGS for chlorination by leaching.

Electrosynthesis of Titanium from High-Titanium Slag with Short-Process in Molten CaCl2

Preparation of Titanium by Electro-deoxidation of CaTiO3 in a Molten CaCl2-NaCl Salt

Preparation of TiC/SiC composites from Ti-enriched slag by an electrochemical process in molten salts

Effective Deoxidation Process of Titanium Scrap Using MgCl2 Molten Salt Electrolytic

Electrochemical extraction of titanium from carbon-doped titanium dioxide precursors by electrolysis in chloride molten salt

Electrolytic synthesis of TiC/SiC nanocomposites from high titanium slag in molten salt

New Method for Low-Cost Titanium Production

Preparation of Titanium Metal by Deoxygenation Under KCl-NaCl-YCl3 System Using Soluble Anode

Carbochlorination of Low-Grade Titanium Slag to Titanium Tetrachloride in Molten Salt

Synthesis of micro-FeTi powders by direct electrochemical reduction of ilmenite in CaCl2-NaCl molten salt

Direct selective extraction of titanium silicide Ti5Si3 from multi-component Ti-bearing compounds in molten salt by an electrochemical process

Chlorination Behavior of Low-Grade Titanium Slag in AlCl3-NaCl Molten Salt

Electrochemical Deoxidation of Titanium and Its Alloy Using Molten Magnesium Chloride

Equilibrium between titanium ions and high-purity titanium electrorefining in a NaCl-KCl melt

A novel preparation of titanium dioxide from titanium slag

Extraction of titanium from different titania precursors by the FFC Cambridge process

Electrode processes in the production of microdispersed titanium powder by volumetric electrolytic reduction of its ions with sodium dissolved in the BaCl2–CaCl2–NaCl melt in the absence of titanium halides in the initial melt

High-Titanium Slag Preparation Process by Carbothermic Reduction of Ilmenite and Wet-Magnetic Separation

Thermodynamic design of electroslag remelting slag for high titanium and low aluminium stainless steel based on IMCT