Abstract:In this paper, a new short process integrating carbochlorination and electrolyzation to produce metallic titanium in molten NaCl–CaCl2 electrolyte was presented. This electrochemical experiment was carried out at 1123 K using carbon-doped TiO2 precursors. The electrolysis process of intermediate produced by carbochlorination of carbon-doped TiO2 precursors was studied. The cathodic product was analyzed using X-ray diffraction (XRD), inductively coupled plasma atomic emission spectroscopy (ICP-AES) and scanning electron microscopy (SEM) after electrolysis. The evolved gas was analyzed by a gas chromatograph equipped with a thermal conductivity detector (GC-TCD). Results showed that Ti powder of 98.7% could be obtained as the final product in the cathode by electrolysis for 5 h at 4.0 V using raw pellets with a C/TiO2 mass ratio of 0.15. Furthermore, the electrochemical process of Ti deposition was comprehensively evaluated by cyclic voltammetry and squarewave voltammetry. The electrode reaction mechanisms and particle evolution principles in molten salt during this electrolysis process were discussed. It indicated that titanium chloride in lower valence (TiCl3) with more productive advantage could exist as an intermediate, and Ti3+ ions were reduced to Ti metal by a two-step mechanism corresponding to the pathway: Ti3+ → Ti2+ → Ti.

Preparation of Ferrotitanium Alloy from Ilmenite by Electrochemical Reduction in Chloride Molten Salts

Preparation of Ferrotitanium from Ilmenite by Electrolysis-Assisted Calciothermic Reduction in CaCl2-NaCl Molten Salt

Electro-Reduction of Ilmenite to Fe<sub>x</sub>Ti Alloys in Molten CaCl<sub>2</sub>

Synthesis of micro-FeTi powders by direct electrochemical reduction of ilmenite in CaCl2-NaCl molten salt

Direct Electro-deoxidation of Ilmenite Concentrate to Prepare FeTi Alloy in CaCl2 Molten Salt

Experimental investigation on the formation mechanism of the TiFe alloy by the molten-salt electrolytic titanium concentrate

Electrolytic Synthesis of Ferrotitanium Powders from Ilmenite in CaCl2-NaCl Melts at a Lower Temperature of 700 °C

Preparation of Titanium by Electro-deoxidation of CaTiO3 in a Molten CaCl2-NaCl Salt

Direct Electrosynthesis of Fe-TiC Composite from Natural Ilmenite in Molten Calcium Chloride

Electrosynthesis of Titanium from High-Titanium Slag with Short-Process in Molten CaCl2

Direct electrochemical reduction of low titanium chlorides into titanium aluminide alloy powders from molten eutectic KCl–LiCl–MgCl2

Electrochemical extraction of titanium from carbon-doped titanium dioxide precursors by electrolysis in chloride molten salt

Preparation of Titanium Deposit in Chloride Melts

Electrochemical synthesis of Ti–Al–V alloy by chlorination of Ti2O3 and V2O3 in AlCl3-containing molten chloride salt

Removal of Iron from Titanium Ore through Selective Chlorination Using Magnesium Chloride

Low Temperature Electrodeposition of Titanium in Fluoride-Added LiCl–KCl–CsCl Molten Salt

Electrochemical Preparation of Ti5Si3/TiC Composite from Titanium-Rich Slag in Molten CaCl2

Equilibrium between titanium ions and high-purity titanium electrorefining in a NaCl-KCl melt

Investigation on the reaction progress of titanium and lead chloride in NaCl-KCl melt

A novel process for preparation of titanium dioxide from Ti-bearing electric furnace slag: NH4HF2-HF leaching and hydrolyzing process