Abstract:Abstract The synthesis, microstructure, and properties of high purity dense bulk Mo 2 TiAlC 2 ceramics were studied. High purity Mo 2 TiAlC 2 powder was synthesized at 1873 K starting from Mo, Ti, Al, and graphite powders with a molar ratio of 2:1:1.25:2. The synthesis mechanism of Mo 2 TiAlC 2 was explored by analyzing the compositions of samples sintered at different temperatures. It was found that the Mo 2 TiAlC 2 phase was formed from the reaction among Mo 3 Al 2 C, Mo 2 C, TiC, and C. Dense Mo 2 TiAlC 2 bulk sample was prepared by spark plasma sintering (SPS) at 1673 K under a pressure of 40 MPa. The relative density of the dense sample was 98.3%. The mean grain size was 3.5 μm in length and 1.5 μm in width. The typical layered structure could be clearly observed. The electrical conductivity of Mo 2 TiAlC 2 ceramic measured at the temperature range of 2–300 K decreased from 0.95 × 10 6 to 0.77 × 10 6 Ω–1·m–1. Thermal conductivity measured at the temperature range of 300–1273 K decreased from 8.0 to 6.4 W·(m·K) –1 . The thermal expansion coefficient (TEC) of Mo 2 TiAlC 2 measured at the temperature of 350–1100 K was calculated as 9.0 × 10 –6 K –1 . Additionally, the layered structure and fine grain size benefited for excellent mechanical properties of low intrinsic Vickers hardness of 5.2 GPa, high flexural strength of 407.9 MPa, high fracture toughness of 6.5 MPa·m 1/2 , and high compressive strength of 1079 MPa. Even at the indentation load of 300 N, the residual flexural strength could hold 84% of the value of undamaged one, indicating remarkable damage tolerance. Furthermore, it was confirmed that Mo 2 TiAlC 2 ceramic had a good oxidation resistance below 1200 K in the air.

Synthesis and characterization of submicro-sized V2AlC ceramics by a two-step modified molten salt method

<i>In Situ</i>Reaction Synthesis and Mechanical Properties of V<sub>2</sub>AlC

Synthesis of Nano Sized Cr2AlC Powders by Molten Salt Method

In Situ Reaction Synthesis And Mechanical Properties Of V2alc

The synthesis of high purity Ti3AlC2 MAX phase via molten salt method

In-situ Synthesis of Nanocrystalline TiC Powders, Nanorods, and Nanosheets in Molten Salt by Disproportionation Reaction of Ti(II) Species

Efficient synthesis of Ti3AlC2 powders with high purity by microwave-assisted molten salt method

Molten salt synthesis of orthorhombic CrB and Cr2AlB2 ceramics

Facile synthesis of hollow Ti3AlC2 microrods in molten salts via Kirkendall effect

Ternary-layered Cr2AlB2 synthesized from Cr, Al, and B powders by a molten salt-assisted method

V2(Al1−xGax)C microrods synthesized through molten-salt show efficient microwave absorption capability

Studies of synthesizing the SiC nanometer powders by chemical vapor reaction

In-situ synthesis of nano SiC particles in Al–Si–C system at 750 °C

A novel simple method to stably synthesize Ti3AlC2 powder with high purity

Influence of (Ta Nb Ti V) C powders synthesized by molten salt at low temperature on densification and properties of high entropy carbide ceramics

In situ synthesis of Al2O3–SiC powders via molten-salt-assisted aluminum/carbothermal reduction method

Combustion synthesis of ternary carbide Ti3AlC2 in Ti–Al–C system

Synthesis, microstructure, and properties of high purity Mo2TiAlC2 ceramics fabricated by spark plasma sintering

In-situ synthesis and microstructural evolution of a SiC reinforced Al-50Si composite exhibiting exceptional thermal properties

Effects of different Ti/C and Al contents on combustion synthesized Ti3AlC2 powders in the Ti-Al-C system

Electrolytic synthesis of TiC/SiC nanocomposites from high titanium slag in molten salt