Abstract:Cr2AlB2 and Cr4AlB4 are members of the MAB phases that exhibit unique properties of both metals and ceramics. However, despite these unique characteristics, Cr2AlB2 and Cr4AlB4 phase coatings have not been widely investigated. In this study, Cr2AlB2 and Cr4AlB4 MAB phase coatings were fabricated by magnetron sputtering at room temperature and post-annealing. A composite target, consisting of a phase-pure disc-shaped CrB target overlapped by uniformly dispersed fan-shaped Al slices, was placed parallel to the substrates. The Al content of the coatings was adjusted by altering the areal proportion of the Al slices. MAB phases have crystallized upon post-annealing the as-deposited coatings on Al2O3(0001) substrates in Ar. The phase compositions and morphologies of the crystalline coatings were found to be dependent on the Al content and the annealing temperature. As-deposited coatings with a Cr:Al:B ratio close to 2:1:2 could crystallize as pure and dense Cr2AlB2 phases within the temperature range of 650–800 °C; higher annealing temperatures resulted in the decomposition of Cr2AlB2, while crystallization at lower temperatures was not evident from X-ray diffraction. As-deposited coatings with a Cr:Al:B ratio close to 3:1:3, despite containing a relatively higher Al content than required by the stoichiometry of Cr4AlB4, exhibited insufficient crystallization of Cr4AlB4 with unknown phases below 840 °C. Higher annealing temperatures resulted in the coexistence of Cr4AlB4 and CrB, indicating that achieving phase-pure and well-crystallized Cr4AlB4 coatings proved challenging, possibly due to the inevitable loss of Al during annealing. The configuration of the composite target and the substrates provides a promising strategy for fabricating phase-pure and dense Cr2AlB2 coatings.

Ternary-layered Cr2AlB2 synthesized from Cr, Al, and B powders by a molten salt-assisted method

Molten salt synthesis of orthorhombic CrB and Cr2AlB2 ceramics

Synthesis of Nano Sized Cr2AlC Powders by Molten Salt Method

Phase Pure and Well Crystalline Cr2AlB2: A Key Precursor for Two-Dimensional CrB

Preparation of Nb3Al Powder by Chemical Reaction in Molten Salts

In-situ Synthesis of Nanocrystalline TiC Powders, Nanorods, and Nanosheets in Molten Salt by Disproportionation Reaction of Ti(II) Species

Effects of Doped Elements (Si, Cr, W and Nb) on the Stability, Mechanical Properties and Electronic Structures of MoAlB Phase by the First-Principles Calculation

Fabrication of Cr2AlB2 and Cr4AlB4 MAB Phase Coatings by Magnetron Sputtering and Post-Annealing

Synthesis and characterization of submicro-sized V2AlC ceramics by a two-step modified molten salt method

Al-Cr Coatings Prepared by Diffusion at Low Temperature and Its Phase Characterization

Analysis on Phase Stability and Mechanical Property of Newly-discovered Ternary Layered Boride Cr<sub>4</sub>AlB<sub>4</sub>

Preparation and Characterization of TiB2/Al3Ti/Al2O3 Composite Nano-powder

Molten Salt Synthesis, Formation Mechanism, and Oxidation Behavior of Nanocrystalline HfB 2 Powders

Synthesis of zirconium boride (ZrB2) rod crystals through salt-assisted boro/carbothermal reduction

Phase Stability and Mechanical Property of Newly-discovered Ternary Layered Boride Cr4AlB4

MS3, physical properties, and formation mechanism of TiV1/3Cr1/3Nb1/3AlC powders: Experimental and first-principles investigation

Preparation of ultrafine (W,Mo)B, (W,Mo)B2.5 and (Mo,W)AlB solid solution composite powders

Synthesis of Ti0.2Zr0.8B2 Solid‐solution Nanopowders by Molten Salt Assisted Borothermal Reduction

Molten-salt Synthesis of BaTiO3 Powders and Their Atomic-Scale Structural Characterization

Effects of Zn and Si on the microstructure evolution of the Cr-Al-B MAB phase contained in the periodic layered structure formed in-situ

Molten Salt Synthesis, Characterization, and Formation Mechanism of Superfine (hfxzr1‐x)b2 Solid‐solution Powders