Abstract:Through defect modulation, ZrB 2 powder was controllably synthesized using the carbon thermal reduction (CTR) method, with boron powder serving as a novel additive. Thermodynamic data for the ZrO 2 -B 2 O 3 -C system in the presence of boron were calculated using HSC thermodynamic software. Additionally, TG-DSC thermal analysis combined with XRD was used to investigate the reaction process. Transmission electron microscopy (TEM) and scanning electron microscopy (SEM) were used to analyze the defect structure and grain surface characteristics of the reaction products. The results indicate that the reaction of B with ZrO 2 and C exothermically alters the nucleation environment of ZrB 2 grains. The helical dislocations generated act as a source of crystal growth steps, promoting the growth of smooth interfaces and leading to a transformation of the ZrB 2 grain growth mechanism. Quantitative calculations of the dislocation density of ZrB 2 powders, using the convolutional multiple whole profile fitting (CMWP-fit), suggest that the inclusion of boron as an additive can modulate the defect concentration of the products. ZrB 2 powders with varied dislocation densities were achieved through meticulously controlled synthesis methods, followed by subsequent densification via hot pressing sintering. The results indicated that the relative density of ZrB 2 ceramics increased from 83.9 % to 96.7 % as the dislocation density of the powder increased from 2.7 × 10 13 m −2 to 7.6 × 10 14 m −2 with the rise in boron content from 0 wt% to 3 wt%. In addition, the defects create extra sintering-driving forces that induce a shift in the densification mechanism from grain boundary diffusion to dislocation slip during hot-pressing sintering. This shift results in an increase in the apparent activation energy from 105 kJ/mol to 210 kJ/mol.

Synthesis of zirconium boride (ZrB2) rod crystals through salt-assisted boro/carbothermal reduction

Highly Efficient and Low-Temperature Preparation of Plate-Like ZrB₂-SiC Powders by a Molten-Salt and Microwave-Modified Boro/Carbothermal Reduction Method.

Carbothermal Reduction Synthesis Of Zirconium Diboride Powders Assisted By Microwave

Fully dense ZrB 2 ceramics by borothermal reduction with ultra‐fine ZrO 2 and solid solution

Effect of ZrB2 on promoting the phase transformation mechanism of Si3N4-based ceramics at low temperature

Synthesis of Ultra-Fine and High-Pure Zirconium Diboride Powders Using Solution-Based Processing

Defect-regulated synthesis of ZrB 2 powders via carbon thermal reduction and elucidation of its hot-pressing densification mechanism

Molten salt synthesis of orthorhombic CrB and Cr2AlB2 ceramics

Molten Salt Synthesis of ZnNb{sub 2}o{sub 6} Powder

Improvement of sinterability and mechanical properties of ZrB2 ceramics by the modified borothermal reduction methods

Improvement of ZrB2 nanopowder synthesis by sol-gel method via zirconium alkoxide/boric acid precursors

Pressureless Sintering of Zirconium Diboride Ceramics with Boron Additive

Enhanced Mechanical Properties and Oxidation Resistance of Zirconium Diboride Ceramics via Grain‐Refining and Dislocation Regulation

Effect of ZrB2 powders on densification, microstructure, mechanical properties and thermal conductivity of ZrB2-SiC ceramics

Monolithic ZrB 2 ‐based UHTC s using polymer‐derived Si(Zr,B)CN as sintering aid

In-situ synthesis of hierarchically high porosity ZrB 2 ceramics from carbon aerogel template with excellent performance in thermal insulation and light absorption

Synthesis of ZrB2-SiC-ZrC Composite Powders with Core-Shell Structure Via Sol-Gel Molecular Modulation

Oxalate-precursor processing for high quality BaZrO3

Influence of TiB2 and CrB2 on densification, microstructure, and mechanical properties of ZrB2 ceramics

Preparation and Mechanical Properties of ZrB2-based Ceramics Using MoSi2 As Sintering Aids

Progress in Preparation of ZrB2 Nanopowders Based on Traditional Solid-State Synthesis