Abstract:In the present study, ZrB2 nanoparticles were synthesized using sol-gel method. Zirconium alkoxide was used as the source of zirconium and boric acid as the source of boron. The size of precursor nanoparticle was controlled using the pH parameter inside the sol, and the formation of primary nuclei of ZrB2 phase and their crystallized amount were investigated using the temperature parameter. To evaluate the mechanism of product formation during the sol-gel process, TEM, SEM, DTA/TG, RAMAN, XRD, FTIR, and DLS methods were used. DLS analysis showed that the size of precursor particle inside the sol at pH less than 5 was below 10 nm. Measurements of viscosity and zeta potential inside the sol showed that in the acidic range, the particle stability decreases with increasing pH. Mixing of precursor particles at molecular level inside the sol was one of the important reasons in reducing the synthesis temperature of ZrB2 particles. FTIR analysis on chemical bonds showed that Zr-O-B bond was formed inside the gel powder. DTA analysis showed that the primary nuclei of ZrB2 particles were formed at a temperature of about 1400 °C. XRD observations proved that the primary nuclei of the ZrB2 phase crystallized and grew at a temperature of about 1500 °C. Surface research revealed that the specific surface area of the synthesized ZrB2 particles is equivalent to 115 m2/g, and also the surfaces of these particles are porous, and the size of these porosities is in meso range. SEM analysis showed that the particle size of ZrB2 having homogeneous morphology is about 50 nm. TEM microstructural analysis revealed that ZrB2 particles were formed uniformly and orderly in very fine dimensions.Graphical abstract

Improvement of ZrB2 nanopowder synthesis by sol-gel method via zirconium alkoxide/boric acid precursors

Synthesis of ZrB 2 nanoparticles by sol-gel method

Preparation of Zirconium Diboride Nanopowders Using Different Zirconium Sources Via Sol-Gel Method

Morphology evolution of ZrB2 nanoparticles synthesized by solgel method

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Synthesis of Ultra-Fine Zirconium Diboride Powders by Sol-Gel and Precursor Pyrolysis Method

Synthesis of ZrB$lt;inf$gt;2$lt;/inf$gt; Nanoparticles by Using Xylitol

Carbothermal Reduction Acted Synergistically with Sol.Gel Method to Synthesize ZrB2 Nanoparticles

Synthesis of Ultrafine ZrB2 Powders by Sol-Gel Process

Preparation of Zirconia Powders by Sol-gel Process

Effects of Gel Aging on Synthesis of Zrb2 Powders

Synthesis of Ti0.2Zr0.8B2 Solid‐solution Nanopowders by Molten Salt Assisted Borothermal Reduction

Nanocarbon-dependent Synthesis of ZrB2 in a Binary ZrO2 and Boron System

Synthesis of Hexagonal-Prism-like ZrB2 by a Sol–gel Route

Ultrafine ZrB2 Ceramic Powders Prepared by a Sol–Gel Method Synergized with a Carbothermic Reaction and Their Improved Sintering Performance

Low Temperature Synthesis of ZrB 2 Powder Synergistically by Borothermal and Carbothermal Reduction

Synthesis of Ultra-fine Zirconium Diboride Powders by Liquid-phase Method

Syntheses of ZrC–SiC Nanopowder Via Sol–gel Method

Sol-gel synthesis and characterization of mesoporous TiB2 nano powder via Titanium isopropoxide /trimethyl borate precursors

ZrO2 Nanoparticles Synthesized by the Sol–Gel Method: Dependence of Size on pH and Annealing Temperature

Preparation of Nano-Zrb2 Powder by Ca Liquid Assisted Boronation Reaction Between ZrC and B4C