Abstract:Despite zirconia (ZrO2) ceramics and lithium disilicate (Li2Si2O5) glass-ceramics have been widely applied on the market for dental restorations, composites that can combine the advantages of both are still demanded. Here we introduced a ZrO2-Li2Si2O5 ceramic with minimized glass phases that fabricated through a sol-gel method and subsequent pressureless sintering. ZrO2-Li2Si2O5 powders were obtained after the gel precursors were heat treated under 800 °C. The gel-derived powders were molded and pressureless sintered under 900-1000 °C to investigate their sintering properties. From the microstructures of the sintered samples, we knew that the densification process was dominated by the growth of Li2Si2O5 grains instead of the growth of ZrO2 grains. Increasing in Li2Si2O5 content can promote ceramic densification. Interestingly, reactions between ZrO2 and Li2Si2O5 were observed with sintering temperature higher than 916 °C, which can increase the porosity of the ceramics. Therefore, both the content of Li2Si2O5 and sintering temperature should be well adjusted to achieve samples with desired properties. Finally, ceramics with flexural strength of 226 MPa and porosity of 0.4% were achieved from powders with moderate Li2Si2O5 content after sintering at 1000 °C.

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Preparation of Ultrafine Spherical Pr-ZrSiO 4 Pigment by Sol-Gel-Microemulsion Method

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

Preparation of Zirconia Powders by Sol-gel Process

Preparation of ZrO2 microspheres by spray granulation

Preparation of spherical zirconia powder by nano-reactor of microemulsion and its densification behavior

Synthesis of Monolithic Zirconia with Macroporous Bicontinuous Structure Via Epoxide-Driven Sol–gel Process Accompanied by Phase Separation

Sol–gel Synthesis of Mesoporous Spherical Zirconia

Preparation of Nano-ZrO2 powder via a microwave-assisted hydrothermal method

Controllable synthesis of (Ba0.85Ca0.15)(Zr0.1Ti0.9)O3 submicron sphere by hydroxide co-precipitation method

Preparation of spherical zirconia powder in microemulsion system and its densification behavior

Preparations and Characterizations of New Mesoporous ZrO2 and Y2O3-stabilized ZrO2 Spherical Powders

Effects of Synthetic Parameters in Pechini Method on the Formation and Properties of (zro2)0.92(sc2o3)0.08 Solid Solution

Synthesis and formation mechanism of ZrC–SiC–TiC ceramic powders with high-sinterability via sol-gel process and carbothermal reduction

Study on a new, environmentally benign method and its feasibility of preparing nanometer zirconia powder

Synthesis and Characterization of Samaria Stabilized Zirconia Powders by Buffer-Solution Method

From modification to mechanism: Supercritical hydrothermal synthesis of nano-zirconia

Mechanochemical dehydration and crystallization of supersaturated zirconia–alumina composite nano powders

Synthesis of ZrB2-SiC-ZrC Composite Powders with Core-Shell Structure Via Sol-Gel Molecular Modulation

Hydrothermal synthesis of (ZrO2)0.86(Sm 2O3)0.14 nano-powders and electrical properties of its sinter

Sol-gel preparation of ZrO2–Li2Si2O5 ceramics and their sintering properties