Sol-gel preparation of ZrO2–Li2Si2O5 ceramics and their sintering properties

Feng Wang,Yiran Shao,Congqin Ning

DOI: https://doi.org/10.1016/j.jmbbm.2021.105032

IF: 4.042

2022-02-01

Journal of the Mechanical Behavior of Biomedical Materials

Abstract:Despite zirconia (ZrO₂) ceramics and lithium disilicate (Li₂Si₂O₅) glass-ceramics have been widely applied on the market for dental restorations, composites that can combine the advantages of both are still demanded. Here we introduced a ZrO₂-Li₂Si₂O₅ ceramic with minimized glass phases that fabricated through a sol-gel method and subsequent pressureless sintering. ZrO₂-Li₂Si₂O₅ powders were obtained after the gel precursors were heat treated under 800 °C. The gel-derived powders were molded and pressureless sintered under 900-1000 °C to investigate their sintering properties. From the microstructures of the sintered samples, we knew that the densification process was dominated by the growth of Li₂Si₂O₅ grains instead of the growth of ZrO₂ grains. Increasing in Li₂Si₂O₅ content can promote ceramic densification. Interestingly, reactions between ZrO₂ and Li₂Si₂O₅ were observed with sintering temperature higher than 916 °C, which can increase the porosity of the ceramics. Therefore, both the content of Li₂Si₂O₅ and sintering temperature should be well adjusted to achieve samples with desired properties. Finally, ceramics with flexural strength of 226 MPa and porosity of 0.4% were achieved from powders with moderate Li₂Si₂O₅ content after sintering at 1000 °C.

engineering, biomedical,materials science, biomaterials