Effect of Si/Zr molar ratio on the sintering and crystallization behavior of zircon ceramics

Zhengdi Jiang,Tianheng Xiong,Zimei Bai,Dandan Zhao,Wenping Yang,Yun Peng,Hui Dan,Yi Ding,Tao Duan

DOI: https://doi.org/10.1016/j.jeurceramsoc.2020.05.043

IF: 5.7

2020-10-01

Journal of the European Ceramic Society

Abstract:<p>Zircon (ZrSiO₄) ceramics have been widely used in the field of radioactive waste immobilization and ceramics industry. However, preparation of zircon ceramics suffers from low yield due to the variable Si/Zr molar ratio. Herein, we reported preparation of <em>x</em>SiO₂/ZrSiO₄ (0≤<em>x</em>≤0.3) ceramics using SiO₂ and ZrO₂ as raw materials. The effects of Si/Zr molar ratio and sintering temperature on the phase formation, phase and microstructure evolutions were investigated. The results indicated that zircon formation efficiency increased with increasing Si/Zr molar ratio from 1 to 1.2, while decreased with increasing Si/Zr molar ratio from 1.2 to 1.3. The as-prepared ceramics with Si/Zr molar ratio of 1.1 and 1.2 were single zircon phase, while with Si/Zr molar ratio of 1 and 1.3 exhibited coexistence of zircon and cristobalite phases. The grain growth and compactness can be enhanced by increasing Si/Zr molar ratio. Furthermore, the relative densities increased with increasing Si/Zr molar ratio.</p>

materials science, ceramics