Abstract:Zirconia‐toughened alumina (ZTA) ceramics with high mechanical properties were sintered by hot‐pressing method using SiC particles (SiCp) and SiC whiskers (SiCw) as the reinforcing agents simultaneously. The influences of sintering temperature, SiCp and SiCw contents on the microstructure and mechanical properties of ZTA ceramics were investigated. It was found that both SiCp and SiCw could contribute to grain refinement significantly and promote the mechanical properties of the ceramics. However, the excess addition of SiCp or SiCw led to the formation of pores with large sizes and degraded the mechanical properties instead. When 13 wt% SiCp was introduced, the maximum flexural strength of 1180.0 MPa and fracture toughness of 15.9 MPa·m1/2 were obtained, whereas the maximum flexural strength of 1314.0 MPa and fracture toughness of 14.7 MPa·m1/2 were achieved at 20 wt% SiCw. Interestingly, the simultaneous addition of SiCp and SiCw could further improve the mechanical properties, and the highest flexural strength of 1334.0 MPa and fracture toughness of 16.0 MPa·m1/2 were achieved at a SiCw/SiCp ratio of 16/4. The reinforcement mechanisms in the ceramics mainly included the phase transformation toughening of ZrO2, the crack deflection and bridging of SiCp and SiCw and the pull‐out of SiCw.

Microstructural evolution and mechanical properties of ZrO<sub>2</sub> (3Y)-Al<sub>2</sub>O<sub>3</sub>-SiC(<sub>w</sub>) ceramics under oscillatory pressure sintering

Optimization of microstructure and mechanical properties of oscillatory pressure sintered ZrO<sub>2</sub>-Al<sub>2</sub>O<sub>3</sub>-SiCp ceramics

Optimization of microstructure and mechanical properties of oscillatory pressure sintered ZrO2–Al2O3-SiCp ceramics

Microstructure and High-Temperature Mechanical Properties of Zro2-Al2o3-Sic Ceramics

Fabrication and Mechanical Properties of ZrO2–Al2O3–SiC(w) Composites by Oscillatory Pressure Sintering

Preparation, mechanical properties, and toughening mechanisms of SiCw/SiCp‐reinforced zirconia‐toughened alumina ceramics

Synergistic strengthening and toughening of oscillatory pressure sintered WC-ZrO2-Al2O3 ceramics

Microstructural evolution and enhanced mechanical properties of 95Al2O3–Yb/Mg/Si ceramics by optimizing sintering temperature

Pressureless Sintering of Silicon Carbide Ceramics Containing Zirconium Diboride

Synergistic Toughening Effect of SiC Whiskers and Particles in ZrO2–Al2O3–SiC Ceramics

Effect Of Sintering Temperature On Structures And Properties Of High Quality Zirconia Ceramics Under Oscillatory Pressure

Improved comprehensive mechanical properties of oscillatory pressure sintered WC–ZrO2–Al2O3 ceramics with VC/Cr3C2 addition

Microstructure and Mechanical Properties of Zirconia Ceramics Consolidated by a Novel Oscillatory Pressure Sintering

Microstructure and Mechanical Properties of Hot-Pressed Al2O3–mullite–ZrO2–SiC Composites

Microstructure and mechanical properties of Zr3Al3C5-based ceramics synthesized by Al-Si melt infiltration

Microstructure and Mechanical Properties of ZTA Composites Fabricated by Oscillatory Pressure Sintering

Microstructure and High Temperature Friction and Wear Properties of Nanostructured ZrO2(Y2O3)-Al2O3 Ceramics

Microstructure and Mechanical Properties of ZrO2-2 Mol% Y2O3 Ceramics

Effects of Y2O3 on microstructure and mechanical properties of ZrB2–SiC ceramics

An Oscillatory Pressure Sintering of Zirconia Powder: Densification Trajectories and Mechanical Properties

Densification, microstructure and mechanical properties of ZrB2–SiCw ceramic composites