Abstract:Zirconia‐toughened alumina (ZTA) ceramics with high mechanical properties were sintered by hot‐pressing method using SiC particles (SiCp) and SiC whiskers (SiCw) as the reinforcing agents simultaneously. The influences of sintering temperature, SiCp and SiCw contents on the microstructure and mechanical properties of ZTA ceramics were investigated. It was found that both SiCp and SiCw could contribute to grain refinement significantly and promote the mechanical properties of the ceramics. However, the excess addition of SiCp or SiCw led to the formation of pores with large sizes and degraded the mechanical properties instead. When 13 wt% SiCp was introduced, the maximum flexural strength of 1180.0 MPa and fracture toughness of 15.9 MPa·m1/2 were obtained, whereas the maximum flexural strength of 1314.0 MPa and fracture toughness of 14.7 MPa·m1/2 were achieved at 20 wt% SiCw. Interestingly, the simultaneous addition of SiCp and SiCw could further improve the mechanical properties, and the highest flexural strength of 1334.0 MPa and fracture toughness of 16.0 MPa·m1/2 were achieved at a SiCw/SiCp ratio of 16/4. The reinforcement mechanisms in the ceramics mainly included the phase transformation toughening of ZrO2, the crack deflection and bridging of SiCp and SiCw and the pull‐out of SiCw.

Fabrication and Mechanical Properties of ZrO2–Al2O3–SiC(w) Composites by Oscillatory Pressure Sintering

Improved Mechanical Properties of Al2O3-25 Vol% SiCw Composites Prepared by Oscillatory Pressure Sintering

Optimization of microstructure and mechanical properties of oscillatory pressure sintered ZrO<sub>2</sub>-Al<sub>2</sub>O<sub>3</sub>-SiCp ceramics

Optimization of microstructure and mechanical properties of oscillatory pressure sintered ZrO2–Al2O3-SiCp ceramics

Synergistic Toughening Effect of SiC Whiskers and Particles in ZrO2–Al2O3–SiC Ceramics

Microstructure and Mechanical Properties of ZTA Composites Fabricated by Oscillatory Pressure Sintering

Fabrication of ZrO2 whisker modified ZrO2 ceramics by oscillatory pressure sintering

Improved Mechanical Properties of 3YSZ Ceramics Prepared by Pressure-less Sintering Assisted by Cold Sintering under Mild Conditions

A Novel Approach to Improve Flexural Strength of Al2O3‐20 Wt% ZrO2 Composites by Oscillatory Pressure Sintering

Synergistic strengthening and toughening of oscillatory pressure sintered WC-ZrO2-Al2O3 ceramics

Enhanced Toughness and Reliability of Si3N4-SiCw Composites under Oscillatory Pressure Sintering

Microstructural evolution and mechanical properties of ZrO<sub>2</sub> (3Y)-Al<sub>2</sub>O<sub>3</sub>-SiC(<sub>w</sub>) ceramics under oscillatory pressure sintering

Preparation of Zirconia Ceramics with High Density and Fine Grains by Oscillatory Pressure Sintering

An Oscillatory Pressure Sintering of Zirconia Powder: Densification Trajectories and Mechanical Properties

Zirconia Ceramics Consolidated by Oscillatory Pressure Sintering and Subsequent Carburization

Mechanical and tribological properties of SiC whiskers reinforced SiC composites via oscillatory pressure sintering

Mechanical and Tribological Properties of SiC Whisker‐reinforced SiC Composites Via Oscillatory Pressure Sintering

Preparation, mechanical properties, and toughening mechanisms of SiCw/SiCp‐reinforced zirconia‐toughened alumina ceramics

Microstructure and Mechanical Properties of Zirconia Ceramics Consolidated by a Novel Oscillatory Pressure Sintering

Preparation and Mechanical Properties of SiC Whisker and Nanosized Mullite Particulate Reinforced TZP Composites

A novel sintering method of Al2O3/SiCw ceramic composites with improved wear resistance: Oscillatory pressure‐assisted sinter forging