Abstract:To fulfill the demands of ceramic components with high strength, high toughness and high reliability in key projects, a novel oscillatory pressure sintering (OPS) method was proposed in this study. With this new method, zirconia ceramics with high relative density, fine grains, high fracture strength, and excellent reliability, were prepared. As a comparison, zirconia ceramics were sintered by pressure -less sintering (PS) method and hot pressing (HP) method at same temperature. SEM analysis shows that the oscillatory pressure inhibits the rapid grain growth of zirconia at high temperature. Statistic results indicate that the OPS zirconia presents fine grain size at 251 nm, while the average sizes of PS and HP zirconia are 451 and 298 nm, respectively. In addition, the oscillatory pressure induces plastic deformation of grains and sliding of grain boundaries, facilitating elimination of closed pores at grain boundaries. As a result, the relative density of OPS zirconia reaches approximately 99.7%. Due to the refinement of grains and the increase in relative density, the OPS zirconia presents an increase from 1003 MPa to 1572 MPa in flexural strength, and an increase from 13 to 32 in Weibull modulus. Furthermore, its resistance to low temperature degradation is also improved because of the microstructure evolution.

Microstructure and Mechanical Properties of Zirconia Ceramics Consolidated by a Novel Oscillatory Pressure Sintering

Preparation of Zirconia Ceramics with High Density and Fine Grains by Oscillatory Pressure Sintering

An Oscillatory Pressure Sintering of Zirconia Powder: Densification Trajectories and Mechanical Properties

Zirconia Ceramics Consolidated by Oscillatory Pressure Sintering and Subsequent Carburization

An Oscillatory Pressure Sintering of Zirconia Powder: Rapid Densification with Limited Grain Growth

Effect Of Sintering Temperature On Structures And Properties Of High Quality Zirconia Ceramics Under Oscillatory Pressure

Effect of Oscillatory Pressure on the Sintering Behavior of ZrO2 Ceramic

Improved Mechanical Properties of 3YSZ Ceramics Prepared by Pressure-less Sintering Assisted by Cold Sintering under Mild Conditions

Optimization of microstructure and mechanical properties of oscillatory pressure sintered ZrO<sub>2</sub>-Al<sub>2</sub>O<sub>3</sub>-SiCp ceramics

Hydrothermal Aging of Zirconia Ceramics Consolidated by Oscillatory Pressure Sintering

Optimization of microstructure and mechanical properties of oscillatory pressure sintered ZrO2–Al2O3-SiCp ceramics

Fabrication of ZrO2 whisker modified ZrO2 ceramics by oscillatory pressure sintering

Microstructure and Mechanical Properties of ZTA Composites Fabricated by Oscillatory Pressure Sintering

A Novel Oscillatory Pressure-Assisted Hot Pressing For Preparation Of Highperformance Ceramics

Enhanced Properties of Pure Alumina Ceramics by Oscillatory Pressure Sintering

Improved Mechanical Properties of Al2O3-25 Vol% SiCw Composites Prepared by Oscillatory Pressure Sintering

Fabrication and Mechanical Properties of ZrO2–Al2O3–SiC(w) Composites by Oscillatory Pressure Sintering

Microstructural evolution and mechanical properties of ZrO<sub>2</sub> (3Y)-Al<sub>2</sub>O<sub>3</sub>-SiC(<sub>w</sub>) ceramics under oscillatory pressure sintering

A Novel Approach to Improve Flexural Strength of Al2O3‐20 Wt% ZrO2 Composites by Oscillatory Pressure Sintering

Silicon Nitride Ceramics Consolidated by Oscillatory Pressure Sintering

Enhanced Toughness and Reliability of Si3N4-SiCw Composites under Oscillatory Pressure Sintering