Abstract:To fulfill the demands of ceramic components with high strength, high toughness and high reliability in key projects, a novel oscillatory pressure sintering (OPS) method was proposed in this study. With this new method, zirconia ceramics with high relative density, fine grains, high fracture strength, and excellent reliability, were prepared. As a comparison, zirconia ceramics were sintered by pressure -less sintering (PS) method and hot pressing (HP) method at same temperature. SEM analysis shows that the oscillatory pressure inhibits the rapid grain growth of zirconia at high temperature. Statistic results indicate that the OPS zirconia presents fine grain size at 251 nm, while the average sizes of PS and HP zirconia are 451 and 298 nm, respectively. In addition, the oscillatory pressure induces plastic deformation of grains and sliding of grain boundaries, facilitating elimination of closed pores at grain boundaries. As a result, the relative density of OPS zirconia reaches approximately 99.7%. Due to the refinement of grains and the increase in relative density, the OPS zirconia presents an increase from 1003 MPa to 1572 MPa in flexural strength, and an increase from 13 to 32 in Weibull modulus. Furthermore, its resistance to low temperature degradation is also improved because of the microstructure evolution.

Improved Mechanical Properties of Al2O3-25 Vol% SiCw Composites Prepared by Oscillatory Pressure Sintering

Enhanced Toughness and Reliability of Si3N4-SiCw Composites under Oscillatory Pressure Sintering

Fabrication and Mechanical Properties of ZrO2–Al2O3–SiC(w) Composites by Oscillatory Pressure Sintering

A Novel Approach to Improve Flexural Strength of Al2O3‐20 Wt% ZrO2 Composites by Oscillatory Pressure Sintering

Optimization of microstructure and mechanical properties of oscillatory pressure sintered ZrO<sub>2</sub>-Al<sub>2</sub>O<sub>3</sub>-SiCp ceramics

Enhanced Properties of Pure Alumina Ceramics by Oscillatory Pressure Sintering

Mechanical and Tribological Properties of SiC Whisker‐reinforced SiC Composites Via Oscillatory Pressure Sintering

Optimization of microstructure and mechanical properties of oscillatory pressure sintered ZrO2–Al2O3-SiCp ceramics

Microstructure and Mechanical Properties of ZTA Composites Fabricated by Oscillatory Pressure Sintering

A novel sintering method of Al2O3/SiCw ceramic composites with improved wear resistance: Oscillatory pressure‐assisted sinter forging

Mechanical and tribological properties of SiC whiskers reinforced SiC composites via oscillatory pressure sintering

Microstructure and Mechanical Properties of SiC-GNPS-SiCW Ceramics by Oscillatory Pressure Sintering

Preparation of Zirconia Ceramics with High Density and Fine Grains by Oscillatory Pressure Sintering

Silicon Nitride Ceramics Consolidated by Oscillatory Pressure Sintering

An Oscillatory Pressure Sintering of Zirconia Powder: Densification Trajectories and Mechanical Properties

Microstructure and Mechanical Properties of Zirconia Ceramics Consolidated by a Novel Oscillatory Pressure Sintering

Oscillatory Pressure Sintering: A New Method for Preparing WC-Co Cemented Carbides

Preparation of graphene nanoplatelets reinforced SiC composites by oscillatory pressure sintering

Zirconia Ceramics Consolidated by Oscillatory Pressure Sintering and Subsequent Carburization

Ultrafine‐grained WC‐based Ceramics Prepared Via Two‐step Oscillatory Pressure Sintering

Synergistic Toughening Effect of SiC Whiskers and Particles in ZrO2–Al2O3–SiC Ceramics