Abstract:In this study, Spark Plasma Sintering (SPS) was utilized to fabricate fine-grained cemented carbides, and an orthogonal experimental design was employed to examine the influence of holding temperature (1100 °C, 1200 °C, 1300 °C) and holding time (5, 10, and 15 min) on the performance of WC-10Co cemented carbide specimens. Compared with conventional sintering methods, this work achieved the production of samples with enhanced overall performance at lower temperatures and shorter durations. Specifically, under the conditions of a holding temperature of 1300 °C and a holding time of 5 min, the resulting specimens exhibited a density of 14.64 g/cm3, a hardness of 91.29 HRA, a fracture toughness of 16.39 MPa·m½, and a transverse rupture strength of 2398 MPa. The microstructural analysis revealed that as the holding temperature increased, the Co phase in the specimens underwent a transformation from its initial powder form to banded cobalt and subsequently to slit-shaped cobalt. It was found that the presence of banded cobalt effectively hinders crack propagation, whereas slit-shaped cobalt is more effective in preventing crack initiation, thus impacting the overall performance of the specimens. By analyzing the sintering curves and microstructures, the densification mechanisms during SPS sintering of WC-Co cemented carbides were elucidated. The study concluded that the state changes of the Co phase play a significant role in the densification behavior, final microstructure, and properties of the sintered material. These findings offer valuable insights for understanding and optimizing the SPS process.

Oscillatory Pressure Sintering: A New Method for Preparing WC-Co Cemented Carbides

Interplay of microstructure and mechanical properties of WC-6Co cemented carbides by hot oscillating pressing method

Preparation of WC-Co Cemented Carbide by Spark Plasma Sintering: Microstructure Evolution, Mechanical Properties and Densification Mechanism

Oscillatory pressure sintering of binderless tungsten carbide

Ultrafine WC-Co cemented carbide with enhanced mechanical properties prepared by oscillating sinter forging

Enhanced Toughness and Reliability of Si3N4-SiCw Composites under Oscillatory Pressure Sintering

Oscillating pressure sintered W-Cu refractory alloy with high density and hardness under lower temperature

Improved Mechanical Properties of Al2O3-25 Vol% SiCw Composites Prepared by Oscillatory Pressure Sintering

Ultrafine‐grained WC‐based Ceramics Prepared Via Two‐step Oscillatory Pressure Sintering

In-Situ Synthesization of WC-6Co Cemented Carbides by SPS

Microstructure and mechanical properties of oscillatory pressure sintered WC ceramics with different carbon sources

Fabrication and Mechanical Properties of ZrO2–Al2O3–SiC(w) Composites by Oscillatory Pressure Sintering

Microstructure and Mechanical Properties of ZTA Composites Fabricated by Oscillatory Pressure Sintering

A facile route to prepare ODS WC Co cemented carbides

Microstructure and properties of WC-12Co cemented carbide fabricated via selective electron beam melting

Zirconia Ceramics Consolidated by Oscillatory Pressure Sintering and Subsequent Carburization

Rapid synthesis of ultrafine WC-Co cemented carbides by in-situ reactions and spark plasma sintering

Microstructure and properties of coarse WC-10CoCrFeMnNi cemented carbide by mechanical alloying and hot pressing sintering

A Novel Approach to Improve Flexural Strength of Al2O3‐20 Wt% ZrO2 Composites by Oscillatory Pressure Sintering

Preparation, properties and microstructure of high hardness WC-co cemented carbide tool materials for ultra-precision machining

Effect of Metal Elements on Microstructure and Mechanical Properties of Ultrafine Cemented Carbide Prepared by SPS