Abstract:WC-Co cemented carbides are widely used in the fields of military, aerospace, mining and cutting industry etc. In this paper, a new two-step method for the preparation of WC-Co cemented carbides was proposed. First, the mixture of yellow tungsten trioxide (WO3) and cobaltic oxide (Co2O3) were reduced by carbon black to remove all the oxygen. Then, the carbothermic reduction products were precisely mixed with an appropriate amount of carbon black to directly prepare WC-Co cemented carbides. The effects of C/WO3 ratio on the phase composition, morphological evolution, particle size and mechanical properties of products are investigated. The experimental results revealed that when the C/WO3 molar ratio was above 2.7, all oxygen in the raw material mixture were removed by carbon black and a mixture of W2C and η-phase were obtained after the first step of carbothermic reduction at 1150 °C for 2 h; then, the mixture of carbothermic reduction product and an appropriate content of carbon black was compacted, and the green compact was first carbonized at 1200 °C for 2 h and then sintered at 1450 °C for 4 h to prepare cemented carbides. With the increase of C/WO3 ratio at the first stage, the content of η-phase with a low melting point increased, which resulted in the large grain size of WC in the finally prepared cemented carbide. Compared with the traditional method of preparing cemented carbides, the cemented carbides prepared by the current method showed a higher hardness and toughness. Furthermore, the addition of a proper content of the VC in the second stage can significantly inhibit the grain growth of WC and further increase the hardness of cemented carbides.

Rapid synthesis of ultrafine WC-Co cemented carbides by in-situ reactions and spark plasma sintering

In-situ synthesis of WC–Co composite powder and densification by sinter-HIP

Synthesis of WC-Co Composite Powder by Reduction and Carbonization Reactions and Its Densification

Ultra-fine Grain Cemented Carbide Fabricated from WC-Co Composite Powder by In-situ Synthesis

A short and facile process to synthesize WC-Co cemented carbides

In-Situ Synthesization of WC-6Co Cemented Carbides by SPS

Preparation of WC-Co Cemented Carbide by Spark Plasma Sintering: Microstructure Evolution, Mechanical Properties and Densification Mechanism

Preparation of WC-6Co Cemented Carbide by SPS's in-site Carbonization

Spark Plasma Sintering of Ultrafine WC-5%Co Cemented Carbide Composite Powders

Fabrication of ultrafine WC-based cemented carbide by spark plasma sintering

Spark Plasma Sintering Of Nanocrystalline Wc/Co Cemented Carbides

Synthesis of WC Composite Powder with Nano-Cobalt Coatings and Its Application in WC-4Co Cemented Carbide

A Novel Route for the Synthesis of Ultrafine WC-15wt %co Cemented Carbides

Research Status of WC-Co Cemented Carbide Prepared by Spark Plasma Sintering

Synthesis of Ultrafine WC-Co Core-shell Composite Powders by Chemical Reduction Method

Synthesis of WC-Co Composite Powders with Two-Step Carbonization and Sintering Performance Study

Spark Plasma Sintering of Fine-Grained WC-Co Composites

Characterizations of Ball-Milled Nanocrystalline WC–Co Composite Powders and Subsequently Rapid Hot Pressing Sintered Cermets

Preparation of Ultrafine WC-10Co Composite Powders by Reduction and Carbonization

A Novel Method for Direct Synthesis of WC-Co Nanocomposite Powder

Enhancement of the mechanical properties of ultrafine-grained WC-Co cemented carbides via the in-situ generation of VC