Abstract:A Co-Ni-Cu multiprincipal element alloy (MPEA) powder was successfully synthesized through coprecipitation. Results of energy dispersive spectroscopy (EDS) and X-ray fluorescence spectroscopy (XRF) revealed nearly equal atomic ratios for Co, Ni, and Cu in the Co-Ni-Cu MPEA powder. Moreover, X-ray diffraction (XRD) confirmed a single-phase face-centered cubic (fcc) structure in the Co-Ni-Cu MPEA powder. To explore the differences in microstructure and mechanical properties, we compared a novel WC-2Co-2Ni-2Cu cemented carbide, utilizing the Co-Ni-Cu MPEA as a binder, with conventional WC-6Co and WC-3Co-3Ni cemented carbides prepared via liquid phase sintering. This comparison was conducted using scanning electron microscopy, XRD, and mechanical properties testing. Observations revealed that the surfaces of WC grains in WC-2Co-2Ni-2Cu and WC-6Co appeared smooth and flat, while those in WC-3Co-3Ni exhibited roughness with numerous terraces. In addition, the average grain size was 0.96, 1.14, and 1.22 mu m in WC-2Co-2Ni-2Cu, WC-6Co, and WC-3Co-3Ni, respectively. Notably, the Co-Ni-Cu MPEA inhibited WC grain growth. WC-2Co-2Ni-2Cu (1388 HV30) exhibited hardness similar to that of WC-6Co (1406 HV30) but the highest fracture toughness (9.04 MPa center dot m(1/2)), while WC-3Co-3Ni (1332 HV30) presented the lowest hardness. Bending strength values were recorded at 2406 MPa for WC-2Co-2Ni-2Cu, 2816 MPa for WC-6Co, and 2645 MPa for WC-3Co-3Ni, with WC-6Co exhibiting the highest bending strength. Considering their microstructures, physical properties, and mechanical properties comprehensively, the novel cemented carbides exhibited only slightly reduced bending strength compared to conventional counterparts. Thus, the Co-Ni-Cu MPEA binder demonstrates promising potential as a replacement for the conventional Co metal binder.

Preparation of low binder WC-Co-Ni cemented carbides with fine WC grains and homogeneous distribution of Co/Ni

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Enhanced the Mechanical Properties and Corrosion Resistance of Ultra-Coarse Grain WC-8Co Cemented Carbides by the Introduction of Cu and Ni

Effects of Ni on the Microstructures and Properties of WC–6Co Cemented Carbides Fabricated by WC–6(Co, Ni) Composite Powders

Preparation of Ultra-Fine WC-Co Cermet and Its Wear Behavior

Ultra-fine Grain Cemented Carbide Fabricated from WC-Co Composite Powder by In-situ Synthesis

Synthesis of WC Composite Powder with Nano-Cobalt Coatings and Its Application in WC-4Co Cemented Carbide

Effect of Cobalt Content on the Microstructure and Mechanical Properties of Coarse Grained WC-Co Cemented Carbides Fabricated from Chemically Coated Composite Powder

Preparation and Properties of WC-TiC-Ni Cemented Carbide

Preparation and Properties of WC-10％ Co Cemented Carbides with Flatter Shape of WC Grains

Synthesis of WC-Co Composite Powder by Reduction and Carbonization Reactions and Its Densification

Microstructures and Properties of WC-10 wt.%CoCrFeNiAlx Composite Cemented Carbides

Ultra-Coarse Grain Wc-Co Cemented Carbide From Chemical Coated Powder By One-Step Hydrogen Reduction

Low temperature pressureless immediate sintering of novel nanostructured WC/Co/NiCrSiB-alloy cemented carbide

Investigation of ultrafine WC-Co-Fe-Ni-Cr<sub>3</sub>C<sub>2</sub> cemented carbide microstructure and properties based on phase diagram thermodynamics

Study on Effect of High-Entropy Alloy Binder on Microstructure and Properties of WC Cemented Carbide Doped with Rare Earth Oxide

Effects of Ni Addition and Cyclic Sintering on Microstructure and Mechanical Properties of Coarse Grained WC–10Co Cemented Carbides

Effects of Ni Addition on Mechanical Properties and Corrosion Behaviors of Coarse-Grained WC-10(Co, Ni) Cemented Carbides

Microstructures and Properties of a Novel Cemented Carbide Prepared Using a Co–Ni–Cu Multiprincipal Element Alloy As the Binder

Effect of Bimodal WC Particle Size and Binder Composition on the Morphology of WC Grains in WC–Co–Ni3Al Cemented Carbides

Effect of Vc and Nbc Additions on Microstructure and Properties of Ultrafine Wc-10co Cemented Carbides