Abstract:While the addition of WC increases the hardness and wear resistance of coatings, an excessive WC content can also induce crack initiation and propagation, increasing brittleness and leading to premature failure. Therefore, in this study, WC particles were incorporated into nickel-based coatings by plasma-arc surfacing to optimize their content and distribution, balancing their tensile properties and wear resistance. The coatings were comprehensively evaluated through microstructural analysis, hardness testing, wear resistance assessment, and tensile testing. The results show that as the mass fraction of WC increased from 45% to 65%, the increase in carbon significantly promoted the formation of M7C3, M6C, and M23C6 carbides and suppressed the formation of the γ-phase. The microstructural analysis showed that the content of massive carbides increased significantly with the increasing WC content, and the XPS analysis further confirmed that the changes in the WC and Cr7C3 phases were particularly pronounced in the high-WC coating. The 65% WC coating showed higher hardness (a 232 increase in HV1.0), a lower and more stable coefficient of friction (0.42), and better wear resistance than the 45% WC coating, with a wear rate of 3.329 × 10−6 mm3/(N·m)−1, which was 3.709 × 10−6 mm3/(N·m)−1 lower than that of the 45% WC coating. The conventional tensile test results show that the maximum stress and strain of the 45% WC coating were 71% and 36% higher than those of the 65% WC coating, respectively. In addition, the 45% WC coating exhibited better ductility and quasi-cleavage characteristics, whereas the 65% WC coating showed typical brittle cracking behavior. The results of the field tensile tests also showed that the fracture time of the 65% WC coating was 27 s shorter than that of the 45% WC coating. Overall, the 45% WC coating had a good combination of strength and toughness.

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Enhanced the Mechanical Properties and Corrosion Resistance of Ultra-Coarse Grain WC-8Co Cemented Carbides by the Introduction of Cu and Ni

Effect of Cr3C2 Addition on Microstructure and Mechanical Properties of WC-CoNiFe Cemented Carbides

Cold-sprayed Cu Matrix Composite Coatings with Core-Shell Structured Co@WC Reinforcements on Q235 Steel

Effect of Co Addition on Solidification Velocity, Hardness and Refined Structure Transformation Mechanisms of Undercooled Ni-Cu-Co Alloys

Influence of Ni and Cr on Anti-corrosion Performance of Tungsten Carbide Base Hard Alloy

Effect of WC addition on microstructure and properties of powder metallurgy CoCrNi medium entropy alloy

Microstructures and Properties of WC-10 wt.%CoCrFeNiAlx Composite Cemented Carbides

Microstructure Evolution and Hardness Improvement of WC-Co Composites Sintered with Fe Substituting Part of Co Binder

Effect of WC-12Co on the mechanical and wear performance of laser melting deposition nickel-based alloy

The Effect of Coating Grain Size on the Selective Oxidation Behaviour of Ni-Cr-Al Alloy

Optimizing Wear Resistance and Tensile Strength of Nickel-Based Coatings through Tungsten Carbide Reinforcement

Study on Effect of High-Entropy Alloy Binder on Microstructure and Properties of WC Cemented Carbide Doped with Rare Earth Oxide

The alloying effects of Cr on in-situ phase evolution and wear resistance of nickel composite coatings fabricated by wide-band laser deposition

Coarse-grained WC–6Co hardmetals with dual-scale and plate-like WC structures fabricated by convention powder metallurgy process

Effects of Ni Addition on the Mechanical and Electrical Properties of Cu-15 Mass%Cr In-Situ Composites

Improvement of high-temperature oxidation resistance of WC–Co–Ni alloy by Cr3C2–CeO2–WS2 mixed additives and its mechanism

Effect of Nano WC on Wear and Corrosion Resistances of CoCrFeNiTi High Entropy Alloy Coating

Effect of carbon content on the microstructure and properties of Cr-doped WC–15Co cemented carbide

Effect of Al content in CoCrFeNiAl x HEA on mechanical properties and high temperature oxidation resistance of WC-10%CoCrFeNiAl x hard alloy

Comparative Study on Microstructure and Mechanical Properties of Coarse-grained WC-based Cemented Carbides Sintered with Ultrafine WC or (W+C) as Additives