Effect of Carbon Content on the Microstructure and Mechanical Properties of Ultrafine WC-15Co Cemented Carbides Using a Co-based Solid Solution Binder Phase
Yachao Huang,Qiumin Yang,Tongzhou Deng,Mingfeng Li,Liyong Chen,Yanyuan Tang,Longhui Zhang,Shaoyi Wang,Guozuan Xu
DOI: https://doi.org/10.1016/j.jallcom.2024.177233
IF: 6.2
2025-01-01
Journal of Alloys and Compounds
Abstract:In this paper, a new method was proposed to improve the uniformity of the distribution of grain-growth inhibitors using a Co-based solid solution prepared with Co3O4, Cr2O3, and V2O5 as the raw materials through hightemperature hydrogen reduction. The effect of carbon content on the microstructure and mechanical properties of ultrafine WC-15Co cemented carbides using a Co-based solid solution binder phase were studied. The results demonstrated that the carbon content exerted a considerable influence on the composition of the binder phase, thereby affecting the morphology of the WC grains. With increasing the carbon content, Cr and V precipitated from the Co-based solid solution, adhering to the habit planes of WC or segregating at the WC-Co interface. This hindered the growth of WC grains, yielding an average particle size smaller than that of alloys containing 6.0 wt % carbon content. However, increased carbon content may enhance grain growth owing to the dissolutionprecipitation process of WC grains during the liquid-phase sintering process. Thus, an alloy comprising 6.31 wt% carbon content and featuring trigonal prismatic-shaped WC grains with a mean particle size of 0.310 mu m exhibited excellent comprehensive performance, characterized by a hardness, transverse rupture strength, and fracture toughness of 1579 kg/mm2, 2581 MPa, and 10.56 MPa & sdot;m1/2, respectively.