Abstract:A Co-Ni-Cu multiprincipal element alloy (MPEA) powder was successfully synthesized through coprecipitation. Results of energy dispersive spectroscopy (EDS) and X-ray fluorescence spectroscopy (XRF) revealed nearly equal atomic ratios for Co, Ni, and Cu in the Co-Ni-Cu MPEA powder. Moreover, X-ray diffraction (XRD) confirmed a single-phase face-centered cubic (fcc) structure in the Co-Ni-Cu MPEA powder. To explore the differences in microstructure and mechanical properties, we compared a novel WC-2Co-2Ni-2Cu cemented carbide, utilizing the Co-Ni-Cu MPEA as a binder, with conventional WC-6Co and WC-3Co-3Ni cemented carbides prepared via liquid phase sintering. This comparison was conducted using scanning electron microscopy, XRD, and mechanical properties testing. Observations revealed that the surfaces of WC grains in WC-2Co-2Ni-2Cu and WC-6Co appeared smooth and flat, while those in WC-3Co-3Ni exhibited roughness with numerous terraces. In addition, the average grain size was 0.96, 1.14, and 1.22 mu m in WC-2Co-2Ni-2Cu, WC-6Co, and WC-3Co-3Ni, respectively. Notably, the Co-Ni-Cu MPEA inhibited WC grain growth. WC-2Co-2Ni-2Cu (1388 HV30) exhibited hardness similar to that of WC-6Co (1406 HV30) but the highest fracture toughness (9.04 MPa center dot m(1/2)), while WC-3Co-3Ni (1332 HV30) presented the lowest hardness. Bending strength values were recorded at 2406 MPa for WC-2Co-2Ni-2Cu, 2816 MPa for WC-6Co, and 2645 MPa for WC-3Co-3Ni, with WC-6Co exhibiting the highest bending strength. Considering their microstructures, physical properties, and mechanical properties comprehensively, the novel cemented carbides exhibited only slightly reduced bending strength compared to conventional counterparts. Thus, the Co-Ni-Cu MPEA binder demonstrates promising potential as a replacement for the conventional Co metal binder.

Effect of binder content and sintering time on the microstructure and mechanical properties of gradient cemented carbides with Ni binder

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Comparison of the microstructure and mechanical properties of WC-Ti(C, N)-Ni gradient cemented carbides prepared by SPS pre-sintering and vacuum pre-sintering

Enhanced the Mechanical Properties and Corrosion Resistance of Ultra-Coarse Grain WC-8Co Cemented Carbides by the Introduction of Cu and Ni

The effect of binder phase content on WC-AlCoCrFeNiTi0.2 high entropy cemented carbides microstructure and mechanical properties

The Effect of Carbon Content on the Microstructure and Mechanical Properties of Cemented Carbides with a CoNiFeCr High Entropy Alloy Binder

Effect of WC grain size on mechanical properties and microstructures of cemented carbide with medium entropy alloy Co-Ni-Fe binder

Study on Effect of High-Entropy Alloy Binder on Microstructure and Properties of WC Cemented Carbide Doped with Rare Earth Oxide

Microstructures and mechanical properties of the bilayer functionally graded WC-TiC-Ni/Co cemented carbides

Sintering behavior of WC-10Co-V(C, N) nanocrystalline gradient cemented carbide

Fabrication of gradient WC-Ni cemented carbide materials by high gravity-assisted combustion synthesis and infiltration

Microstructures and Properties of a Novel Cemented Carbide Prepared Using a Co–Ni–Cu Multiprincipal Element Alloy As the Binder

Effects of Lower Cobalt Binder Concentrations in Sintering of Tungsten Carbide

Preparation of low binder WC-Co-Ni cemented carbides with fine WC grains and homogeneous distribution of Co/Ni

L1 2 strengthening of WC-CoNiFe cemented carbides by spark plasma sintering

Effect of initial WC particle size on grain growth behavior and gradient structure formation of bilayer functionally graded cemented carbides

Effect of the carbon content on the morphology evolution of the η phase in cemented carbides with the CoNiFeCr high entropy alloy binder

Effect of the nitrogen multi-sources on the microstructure and hardness of the graded surface layer in WC–Co–Cubic cemented carbides

Role of V(C, N) on gradient structure formation and mechanical properties of nanocrystalline cemented carbides

Microstructures and Properties of WC-10 wt.%CoCrFeNiAlx Composite Cemented Carbides

Effects of nanocomposite grain growth inhibitors and multi-walled carbon nanotubes on the microstructure and mechanical properties of ultrafine cemented carbides