Enhanced the Mechanical Properties and Corrosion Resistance of Ultra-Coarse Grain WC-8Co Cemented Carbides by the Introduction of Cu and Ni

Wei Su,Rui Xie,Wei Luo,Xin Tang,Ronghua Zhu

DOI: https://doi.org/10.1016/j.matlet.2024.137567

IF: 3

2025-01-01

Materials Letters

Abstract:This work investigated the microstructure and properties evolution of ultra-coarse grain WC-8Co cemented carbides with 0.8 wt% Cu and various Ni contents. The results showed that the simultaneous introduction of Cu and Ni could enhance the mechanical properties and corrosion resistance of ultra-coarse grain WC-8Co cemented carbide. After adding 0.8 wt% Cu and 0.8 wt% Ni, the hardness, strength and fracture toughness of WC-8Co alloy increased from 87.5 HRA, 1923 MPa and 17.05 MPa center dot m1/2 to 87.7 HRA, 2280 MPa and 19.47 MPa center dot m1/2, respectively. Moreover, the corrosion current densities of WC-6.4Co0.8Cu0.8Ni alloy were 12.59 mu A center dot cm- 2 in 0.1 M H2SO4 and 2.26 mu A center dot cm- 2 in 0.1 M NaOH, respectively, which were lower than those of WC-8Co alloy (23.24 mu A center dot cm- 2 and 2.34 mu A center dot cm- 2). In this regard, the introduction of Cu and Ni could save cobalt resources while improving the performance of ultra-coarse grain WC-8Co cemented carbides.