Abstract:In this paper, the influences of Cr3C2/VC content on WC grain size, WC grain shape and mechanical properties of WC–6 wt. % Co cemented carbides were investigated. The results showed that the grain size first rapidly decreased and then slightly decreased with the increasing Cr3C2/VC content, and VC led to finer grain size and narrower size distribution. HRTEM/EDS analysis of the WC/Co interface indicates that the segregation concentration of V is much larger than that of Cr, which may be a strong response to the higher inhibition efficiency of VC. The addition of Cr3C2 induced triangular prism shape WC grains while VC generated stepped triangular prism grains. Despite the grain growth inhibitor (GGI) mechanisms of Cr3C2/VC have been extensively studied in the literature, the doping amount, especially the doping limit, has not been systematically investigated. In this work, the saturated solubilities of Cr and V in cobalt binder phase along with carbon content hare been predicted based on thermodynamic calculations. Based on the theoretical calculations, the doping amount of Cr3C2/VC is designed to be gradually increasing until more or less over their maximum solubilities in the binder phase, thereby investigating the subsequent microstructure and mechanical properties. When the doping of Cr3C2/VC exceeds the maximum solubility in Co phase, Co-rich Cr-carbides and Co-deficient V-carbides would form respectively, which were detrimental to the transverse rupture strength (TRS) and impact toughness. The hardness increased with the increasing Cr3C2/VC content, while the fracture toughness decreased with the increasing Cr3C2/VC content. The TRS initially enhanced and then declined, but the stepped triangular prism shape grains and low fraction of WC/Co interface in WC–6Co–VC cemented carbide led to a more pronounced decline in the TRS. The sample with 0.6 wt. % Cr3C2 addition had good comprehensive mechanical properties, its hardness, fracture toughness and TRS were 1880 kg/mm2, 9.32 MPa·m1/2 and 3450 MPa, respectively.

Influence of Ru content on mechanical, corrosion and oxidation behaviors of WC-15Co cemented carbides

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Enhanced the Mechanical Properties and Corrosion Resistance of Ultra-Coarse Grain WC-8Co Cemented Carbides by the Introduction of Cu and Ni

Influence of Ru on the microstructure and performance of WC-Co cemented carbides

Effect of Cr3C2 Addition on Microstructure and Mechanical Properties of WC-CoNiFe Cemented Carbides

High-temperature mechanical performance of Ru doped cermets

Effect of Cu and CeO2 additives on structure and performance of WC-10Co cemented carbides

Microstructure and properties of ultrafine WC–Co–VC cemented carbides with different Co contents

Influence of Re addition amount on structure, mechanical, oxidation as well as corrosion behaviors of WC-15Co cemented carbide

Effects of Ni and Cu Additions on Microstructures, Mechanical Properties and Wear Resistances of Ultra-Coarse Grained WC–6Co Cemented Carbides

Influence of Cr3C2 and VC Content on WC Grain Size, WC Shape and Mechanical Properties of WC–6.0 wt. % Co Cemented Carbides

High-temperature oxidation-wear properties of Ru-doped cermet

The optimization of mechanical property and corrosion resistance of WC-6Co cemented carbide by Mo2C content

Effect of carbon content on the microstructure and properties of Cr-doped WC–15Co cemented carbide

On the Enhanced Wear Resistance of Ultra-Coarse WC-Co Cemented Carbides by WCoB Addition

Effect of carbon content on the properties of inhomogeneous cemented carbides with fine-grained structures produced via one-step transformation

Influence of Ru-addition on thermal decomposition and oxidation resistance of TiAlN coatings

Study on preparation and properties of WC-8Co cemented carbide doped with rare earth oxide

Enhanced high temperature mechanical properties of WC-Co cemented carbides by VC addition

Comparative Study on Microstructure and Mechanical Properties of Coarse-grained WC-based Cemented Carbides Sintered with Ultrafine WC or (W+C) as Additives

Influences of Cr contents on oxidation behavior of WC-Co-Ni-Cr cemented carbides at 900 °C