Abstract:The corrosion behavior of functionally graded cemented carbide (FGCC), with CoNiCrFe binder (WC-CoNiCrFe), has been investigated by performing electrochemical measurements and chemical characterization. The results showed that the CoNiCrFe binder was selectively dissolved in alkaline and acidic solutions. In the NaOH solution, the high contents of Ni and Co generated a passive film consisting of Co(OH) 2 , Ni(OH) 2 , Co 3 O 4 , and NiO that effectively isolated the corrosive medium from the materials. However, the contents of Fe and Cr were too low to provide satisfactory protection. In the HCl solution, the Cr element generated Cr 0 , Cr 2 O 3 , and Cr(OH) 3 . However, the Cr content was too low to form a passive film. In addition, Co, Ni and Fe in the binder were selectively dissolved in the acidic solution. Moreover, compared with the FGCC, the non-graded cemented carbide (CC) had a higher binder content and a more dispersed WC distribution. Thus, it formed a denser and thicker passive film, which was beneficial for the corrosion resistance in the NaOH solution. However, the CoNiCrFe binder was severely corroded in the HCl solution, which was due to the absence of a passive film. In comparison, the FGCC with a lower binder content and a denser WC distribution, showed a higher corrosion resistance. On the other hand, the WC grain size showed the opposite effect in alkaline and acidic solutions. In the NaOH solution, a small WC grain size increased the number of WC/CoNiCrFe interfaces, which favored the formation of a dense passive film. It, thereby reduced the probability for pitting corrosion. In the HCl solution, the corrosion generally started from grain boundaries with high interface energy as no passive film existed. Thus, a large WC grain size facilitated the improvement of the corrosion resistance. The results from the present study do not only provide a theoretical guidance for an understanding of the anticorrosion mechanism of WC-CoNiCrFe, but also a new approach for the preparation of cemented carbides with high corrosion resistance.

Microstructures and mechanical properties of the bilayer functionally graded WC-TiC-Ni/Co cemented carbides

Effect of initial WC particle size on grain growth behavior and gradient structure formation of bilayer functionally graded cemented carbides

Enhanced the Mechanical Properties and Corrosion Resistance of Ultra-Coarse Grain WC-8Co Cemented Carbides by the Introduction of Cu and Ni

Effect of the nitrogen multi-sources on the microstructure and hardness of the graded surface layer in WC–Co–Cubic cemented carbides

Preparation of a novel dual structure graded cemented carbides induced by bidirectional diffusion

Sintering behavior of WC-10Co-V(C, N) nanocrystalline gradient cemented carbide

Effect of binder content and sintering time on the microstructure and mechanical properties of gradient cemented carbides with Ni binder

Development of multilayer graded cemented carbides with Ti–Zr carbonitride miscibility gaps

Fabrication and performance of graded ultrafine WC–Co cemented carbide tool by one/two-step spark plasma sintering

Relation between the nitrogen gas pressure and structure characteristics of WC–Ti(C, N)–Co graded cemented carbides

Fabrication of gradient WC-Ni cemented carbide materials by high gravity-assisted combustion synthesis and infiltration

Microstructure and mechanical properties of WC–Co-based cemented carbide with bimodal WC grain size distribution

Comparison of the microstructure and mechanical properties of WC-Ti(C, N)-Ni gradient cemented carbides prepared by SPS pre-sintering and vacuum pre-sintering

Effect of WC grain size on mechanical properties and microstructures of cemented carbide with medium entropy alloy Co-Ni-Fe binder

Fabrication and Micro-Structure of a Multilayer Functionally Graded (wc–co)–ni Composite

Effect of MWCNTs on microstructure and properties of WC-9Co gradient cemented carbides

Role of V(C, N) on gradient structure formation and mechanical properties of nanocrystalline cemented carbides

Corrosion behavior of functionally graded cemented carbides with CoNiCrFe binder

Oxidation behavior of functionally graded cemented carbides with CoNiFeCr multi-principal-element alloy binder

Microstructures and Properties of a Novel Cemented Carbide Prepared Using a Co–Ni–Cu Multiprincipal Element Alloy As the Binder

Microstructures and Properties of WC-10 wt.%CoCrFeNiAlx Composite Cemented Carbides