Abstract:The in-situ preparation of WC-6Co composite powder was subjected to dry-bag type cold iso-static pressing without any pre-treatment (The pressing pressure was 1x 10(8) Pa and the holding time was 15 s). Ultra-fine YG6 cemented carbide was prepared by sintering the pressed blank in a low-pressure sintering furnace at a sintering temperature of 1360 degrees C for40 min, and it was kept under 5 MPa pressure holding for 20 min. The morphology, metallography and physical mechanics properties of the YG6 cemented carbide were analyzed. The results show that abnormal grain growth can be observed from the ultra-fine YG6 cemented carbide, and the average grain size of the WC alloy is 0.8 mu m. The hardness (HV30) is (21500 +/- 100) MPa, which is higher than that of the conventional ultra-fine YG6X cemented carbide. Then, the composite powder of WC-6Co was used to produce ultra-fine size YG6 cemented carbide by processes of wet-milling, pressure type spray drying, binder adding, extrusion forming, and low-pressure sintering. The effects of different grain growth inhibitor ratios, ball-milling time, extrusion pressure and sintering temperature on the properties of the alloy were investigated. The results show that when 0.3 wt% VC and 0.8 wt% Cr3C2 are added, wet milling time is 48 h, extrusion is at 24 MPa pressure and sintering temperature is 1340 degrees C, the produced ultra-fine YG6 cemented carbide has homogeneous WC grain size, and no WC grains with abnormal growth can be observed from the OM image of the YG6 cemented carbide. The average grain size of WC alloy is 0.4 mu M, and the grains are in polygonal shapes with relatively round outlines. The strength and hardness of YG6 cemented carbide prepared under these conditions are the highest. The TRS of YG6 cemented carbide is (2250 +/- 20) MPa, and the hardness (HV30) is (22600 +/- 100) MPa. Intergranular fracture, along the WC and WC grain boundary fracture or WC and Co grain boundary fracture can be observed from the morphology of fractures.

Synthesis of Y2O3-doped WC-Co powders by wet chemical method and its effect on the properties of WC-Co cemented carbide alloy

Effect of Y2O3 on microstructure and mechanical properties of WC-Co-cemented carbides prepared via solid-liquid doping method and spark plasma sintering

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Study on preparation and properties of WC-8Co cemented carbide doped with rare earth oxide

Enhanced the Mechanical Properties and Corrosion Resistance of Ultra-Coarse Grain WC-8Co Cemented Carbides by the Introduction of Cu and Ni

Study on Effect of High-Entropy Alloy Binder on Microstructure and Properties of WC Cemented Carbide Doped with Rare Earth Oxide

Microstructure and wear performance of a WC-8Co hard alloy modified using W powders doped with Y 2 O 3

Microstructure and wear performance of a WC-8Co hard alloy modified using W powders doped with Y<sub>2</sub>O<sub>3</sub>

Change of interfacial structure between the matrix and second phase of Y–Zr-modified WC-8Co cemented carbide

Enhancement of the mechanical properties of ultrafine-grained WC-Co cemented carbides via the in-situ generation of VC

Preparation of Ultra-Fine WC-Co Cermet and Its Wear Behavior

Microstructures and Properties of WC-10 wt.%CoCrFeNiAlx Composite Cemented Carbides

Study on Elemental Composition and Interfacial Structure of the Second Phase in WC-8Co Hard Alloy Doped with Rare Earth Components

The optimization of mechanical property and corrosion resistance of WC-6Co cemented carbide by Mo2C content

Effect of Cr3C2 Addition on Microstructure and Mechanical Properties of WC-CoNiFe Cemented Carbides

A short and facile process to synthesize WC-Co cemented carbides

Effect of carbon content on the properties of inhomogeneous cemented carbides with fine-grained structures produced via one-step transformation

In-situ Preparation of Ultra-fine YG6 Cemented Carbide via Sintering of WC-6Co Composite Powder

Effects of micro/nano CeO2 on the microstructure and properties of WC-10Co cemented carbides

Effect of Cu and CeO2 additives on structure and performance of WC-10Co cemented carbides

Microhomogeneous WC-TiC-Co composite powders with enhanced sinterability via a two-step carburization method