Abstract:The in-situ preparation of WC-6Co composite powder was subjected to dry-bag type cold iso-static pressing without any pre-treatment (The pressing pressure was 1x 10(8) Pa and the holding time was 15 s). Ultra-fine YG6 cemented carbide was prepared by sintering the pressed blank in a low-pressure sintering furnace at a sintering temperature of 1360 degrees C for40 min, and it was kept under 5 MPa pressure holding for 20 min. The morphology, metallography and physical mechanics properties of the YG6 cemented carbide were analyzed. The results show that abnormal grain growth can be observed from the ultra-fine YG6 cemented carbide, and the average grain size of the WC alloy is 0.8 mu m. The hardness (HV30) is (21500 +/- 100) MPa, which is higher than that of the conventional ultra-fine YG6X cemented carbide. Then, the composite powder of WC-6Co was used to produce ultra-fine size YG6 cemented carbide by processes of wet-milling, pressure type spray drying, binder adding, extrusion forming, and low-pressure sintering. The effects of different grain growth inhibitor ratios, ball-milling time, extrusion pressure and sintering temperature on the properties of the alloy were investigated. The results show that when 0.3 wt% VC and 0.8 wt% Cr3C2 are added, wet milling time is 48 h, extrusion is at 24 MPa pressure and sintering temperature is 1340 degrees C, the produced ultra-fine YG6 cemented carbide has homogeneous WC grain size, and no WC grains with abnormal growth can be observed from the OM image of the YG6 cemented carbide. The average grain size of WC alloy is 0.4 mu M, and the grains are in polygonal shapes with relatively round outlines. The strength and hardness of YG6 cemented carbide prepared under these conditions are the highest. The TRS of YG6 cemented carbide is (2250 +/- 20) MPa, and the hardness (HV30) is (22600 +/- 100) MPa. Intergranular fracture, along the WC and WC grain boundary fracture or WC and Co grain boundary fracture can be observed from the morphology of fractures.

In-Situ Synthesization of WC-6Co Cemented Carbides by SPS

Preparation of WC-Co Cemented Carbide by Spark Plasma Sintering: Microstructure Evolution, Mechanical Properties and Densification Mechanism

Rapid synthesis of ultrafine WC-Co cemented carbides by in-situ reactions and spark plasma sintering

Spark Plasma Sintering of Ultrafine WC-5%Co Cemented Carbide Composite Powders

Effects of SiC addition on microstructure and properties of WC–6Co cemented carbide prepared by SPS

Oscillatory Pressure Sintering: A New Method for Preparing WC-Co Cemented Carbides

Spark Plasma Sintering Of Nanocrystalline Wc/Co Cemented Carbides

Enhancement of the mechanical properties of ultrafine-grained WC-Co cemented carbides via the in-situ generation of VC

Combined effect of SiC and carbon on sintering kinetics, microstructure and mechanical properties of fine-grained binderless tungsten carbide

Spark Plasma Sintering of Fine-Grained WC-Co Composites

A short and facile process to synthesize WC-Co cemented carbides

Synthesis of Y2O3-doped WC-Co powders by wet chemical method and its effect on the properties of WC-Co cemented carbide alloy

In-situ Preparation of Ultra-fine YG6 Cemented Carbide via Sintering of WC-6Co Composite Powder

Preparation of low binder WC-Co-Ni cemented carbides with fine WC grains and homogeneous distribution of Co/Ni

L1 2 strengthening of WC-CoNiFe cemented carbides by spark plasma sintering

Fabrication of WC-12Co cemented carbide by microwave sintering

Low temperature pressureless immediate sintering of novel nanostructured WC/Co/NiCrSiB-alloy cemented carbide

Effect of Metal Elements on Microstructure and Mechanical Properties of Ultrafine Cemented Carbide Prepared by SPS

Effects of in situ phase reaction of η M12C and M6C on microstructure and mechanical properties of tungsten heavy alloy via spark plasma sintering

Interplay of microstructure and mechanical properties of WC-6Co cemented carbides by hot oscillating pressing method

Synthesis of W-TiC composite powders by wet-chemical process and its sintering behavior by SPS