Abstract:Method of soft metal (Cu) strengthening of Ti3SiC2 was conducted to increase the hardness and improve the wear resistance of Ti3SiC2. Ti3SiC2/Cu composites containing 15 vol.% Cu were fabricated by Spark Plasma Sintering (SPS) in a vacuum. The effect of the sintering temperature on the phase composition, microstructure and mechanical properties of the composites was investigated in detail. The as-synthesized composites were thoroughly characterized by scanning electron micrography (SEM), optical micrography (OM) and X-ray diffractometry (XRD), respectively. The results indicated that the constituent of the Ti3SiC2/Cu composites sintered at different temperatures included Ti3SiC2, Cu3Si and TiC. The formation of Cu3Si and TiC originated from the reaction between Ti3SiC2 and Cu, which was induced by the presence of Cu and the de-intercalation of Si atoms Ti3SiC2. OM analysis showed that with the increase in the sintering temperature, the reaction between Ti3SiC2 and Cu was severe, leading to the Ti3SiC2 getting smaller and smaller. SEM measurements illustrated that the uniformity of the microstructure distribution of the composites was restricted by the agglomeration of Cu, controlling the mechanical behaviors of the composites. At 1000 °C, the distribution of Cu in the composites was relatively even; thus, the composites exhibited the highest density, relatively high hardness and compressive strength. The relationships of the temperature, the current and the axial dimension with the time during the sintering process were further discussed. Additionally, a schematic illustration was proposed to explain the related sintering characteristic of the composites sintered by SPS. The as-synthesized Ti3SiC2/Cu composites were expected to improve the wear resistance of polycrystalline Ti3SiC2.

Synthesis of W-TiC composite powders by wet-chemical process and its sintering behavior by SPS

Fabrication of W–1 Wt.% TiC Composites by Spark Plasma Sintering

Densification and microstructure evolution of W-TiC-Y2O3 during spark plasma sintering

Preparation and Characteristics of W–1 Wt.% TiC Alloy Via a Novel Chemical Method and Spark Plasma Sintering

In-situ synthesis TiC + TiB/Ti composites by spark plasma sintering

Synthesis and Formation Mechanism of W/TiC Composite Powders by a Wet Chemical Route

The microstructure and deformation behavior of W-SiC composites via spark plasma sintering

Activation Pretreatment of W-1.5wt％TiC Composite Powder and Its Sintering Behavior

Preparation and organization of W-Ni/TiC composite material

Preparation and Characterization of Tic-Sic Composites Sintered by Sps

Spark Plasma Sintering of Ultrafine WC-5%Co Cemented Carbide Composite Powders

Microstructure, Mechanical Properties, and Sintering Behavior of Ti3O-Fe2TiO4-TiC Composites

Microstructure and Performances of W–TiC–Y2O3 Composites Prepared by Mechano-Chemical and Wet-Chemical Methods

Densification, Microstructure and Mechanical Performance of TiC/Fe Composites by Spark Plasma Sintering

Rapid synthesis of ultrafine WC-Co cemented carbides by in-situ reactions and spark plasma sintering

Microstructure and Mechanical Properties of Composites Obtained by Spark Plasma Sintering of Ti3SiC2-15 vol.%Cu Mixtures

Microstructure, densification and mechanical properties of in situ TiBw/Ti2AlNb composites fabricated by spark plasma sintering

Combined effect of SiC and carbon on sintering kinetics, microstructure and mechanical properties of fine-grained binderless tungsten carbide

Preparation and Properties of Fine-Grained and Ultrafine-Grained W-TiC-Y2O3 Composite

Reaction mechanism and friction behavior of an in-situ Ti/B4C composite synthesized by spark plasma sintering

Microstructure Characterization of the Cu-Ti-C Composites Prepared by Mechanical Alloying and Spark Plasma Sintering