Abstract:The paper presents the influence of the temperature of the sintering process on the microstructure and selected properties of boron carbide/TiB2/SiC composites obtained in situ by spark plasma sintering (SPS). The homogeneous mixture of boron carbide and 5% vol. Ti5Si3 micropowders were used as the initial material. Spark plasma sintering was conducted at 1700 °C, 1800 °C, and 1900 °C for 10 min after the initial pressing at 35 MPa. The heating and cooling rate was 200 °C/min. The obtained boron carbide composites were subjected to density measurement, an analysis of the chemical and phase composition, microstructure examination, and dry friction-wear tests in ball-on-disc geometry using WC as a counterpart material. The phase compositions of the produced composites differed from the composition of the initial powder mixture. Instead of titanium silicide, two new phases appeared: TiB2 and SiC. The complete disappearance of Ti5Si3 was accompanied by a decrease in the boron carbide content of the stoichiometry formula B13C2 and an increase in the content of TiB2, while the SiC content was almost constant. The relative density of the obtained boron carbide composites, as well as their hardness and resistance to wear, increased with the sintering temperature and TiB2 content. Unfortunately, the reactions occurring during sintering did not allow us to obtain composites with high density and hardness. The relative density was 76–85.2% of the theoretical one, while the Vickers hardness was in the range of 4–12 GPa. The mechanism wear of boron carbide composites tested in friction contact with WC was abrasive. The volumetric wear rate (Wv) of composites decreased with increasing sintering temperature and TiB2 content. The average value of coefficient of friction (CoF) was in the range of 0.54–0.61, i.e., it did not differ significantly from the value for B4C sinters.

Reaction mechanism and friction behavior of an in-situ Ti/B4C composite synthesized by spark plasma sintering

Microstructure and Wear-resistant Properties of in situ TiB-TiC Reinforced Titanium Matrix Composites by Laser Deposition Manufacturing

Spark Plasma Sintering Preparation of Tungsten Carbide-Reinforced Iron-Based Composite Materials: Wear Resistance Performance and Mechanism

Microstructure and mechanical behaviour of transient liquid phase spark plasma sintered B4C–SiC–TiB2 composites from a B4C–TiSi2 system

The Microstructure, Mechanical, and Friction-Wear Properties of Boron Carbide-Based Composites with TiB2 and SiC Formed In Situ by Reactive Spark Plasma Sintering

Toughening mechanism of B4C/TiB2 ceramic materials by in situ reaction via spark plasma sintering

B4C‒TiB2 composite with modified microstructure and enhanced properties from optimal size coupling of raw powders

Planar shock compression of spark plasma sintered B4C and B4C–TiB2 ceramic composites

Densification and strengthening mechanism in spark plasma sintering of B4C–VB2 ceramics via carbide boronizing

Enhancement mechanical properties of in-situ preparated B4C-based composites with small amount of (Ti3SiC2+Si)

Preparation of TiB2–SiC composites toughened with interlocking microstructure by self-assembled TiB2 plates

Microstructure, Mechanical Properties, and Sintering Behavior of Ti3O-Fe2TiO4-TiC Composites

Densification, Microstructure and Mechanical Performance of TiC/Fe Composites by Spark Plasma Sintering

Microstructure evolution, mechanical properties, and wear behavior of in-situ TiCx/TC4 composites

Spark plasma sintering of hard wear‐resistant graphene nanoplatelet–reinforced TiB2 + SiC composites from TiC–B4C–SiC

In-situ synthesized phases during the spark plasma sintering of g-C3N4 added TiB2 ceramics: A thermodynamic approach

Evaluation of the Wear and Mechanical Properties of Titanium Diboride-Reinforced Titanium Matrix Composites Prepared by Spark Plasma Sintering

Effects of TiB2 Particles on the Microstructure Evolution and Mechanical Properties of B4C/TiB2 Ceramic Composite

Microstructure and Mechanical Properties of Composites Obtained by Spark Plasma Sintering of Ti3SiC2-15 vol.%Cu Mixtures

Effects of Boron Content on the Microstructure and Properties of BxC-TiB2 (x=4.5, 6.5 or 8.5) Ceramic Composites by the Reactive Spark Plasma Sintering

Microstructures and mechanical properties of TiB2 composite ceramics with co-addition of Ti and TiC fabricated by SPS