Microstructure evolution, mechanical properties, and wear behavior of in-situ TiCx/TC4 composites

Xinjian Cao,Xiao Liu,Zhongkan Ren,Jie Guo,Xiaoyang Yi,Haizhen Wang,Jun Yang

DOI: https://doi.org/10.1016/j.vacuum.2023.112516

IF: 4

2023-08-21

Vacuum

Abstract:In this work, In-situ TiCx/TC4 composites were fabricated using Ti 3 AlC 2 as a precursor via vacuum hot-pressing sintering. The effect of Ti 3 AlC 2 content on the microstructure, mechanical properties , and wear behavior of TC4 matrix composites was investigated. The results indicate that the TiCx phase formed from the reaction between Ti 3 AlC 2 and Ti during sintering. The in-situ formation of the TiCx phase could refine the size of the prior β grain and alter the microstructures of the matrix from the Widmanstatten structure of neat TC4 to an equiaxed structure. The TC4 matrix composites with different amounts of Ti 3 AlC 2 exhibited higher hardness, yield strength, and tensile strength than neat TC4. When the volume fraction of Ti 3 AlC 2 was 2.5%, the yield strength and tensile strength of composites were 951.2 MPa and 1033 MPa, respectively, which increased by 16.5% and 9.4% compared to neat TC4, respectively. Moreover, the elongation of the composites was 12.8% with substantially maintained plasticity. The improvement of yield strength in the composites is attributed to grain refinement strengthening and load transfer strengthening. The wear behavior of in-situ TiCx/TC4 composites was enhanced significantly. Abrasive wear and adhesive wear are the dominant wear mechanism in the TiCx/TC4 composites.

materials science, multidisciplinary,physics, applied