Fabrication of WC-12Co cemented carbide by microwave sintering

YANG Ya-jie,YI Jian-hong,BAO Rui,LUO Shu-dong,CHEN Gang
DOI: https://doi.org/10.3969/j.issn.1673-0224.2010.01.016
2010-01-01
Abstract:Microwave sintering technique was used to consolidate WC-12Co hard alloy,and the effects of sintering temperature and holding time of temperature on the density,hardness and microstructure of the prepared hard alloy were studied to enhance its performance and decrease the production cost. It is obvious that the WC grains grow slightly,the density and hardness of the alloys is increasing. Experiment evidently shows that the alloys with relative density as high as 99.8%,HRA 87.5 and homogeneous microstrue as well could be achieved when sintered at 1 475 ℃ without holding stage and the overall sintering cycle is in the range of 1.5?2 hours. However the abnormal grain growth and Co phase inhomogeneous distribution are observed,which cause decreasing of density and hardness,in case of temperature holding over than 30 min. Temperature gradient in samples is depressed after using auxiliary heating material/thermal insulator and placing samples properly,and as a consequence the sintered parts remain a good geometrical shape.
What problem does this paper attempt to address?