Abstract:WC-Co cemented carbides are widely used in the fields of military, aerospace, mining and cutting industry etc. In this paper, a new two-step method for the preparation of WC-Co cemented carbides was proposed. First, the mixture of yellow tungsten trioxide (WO3) and cobaltic oxide (Co2O3) were reduced by carbon black to remove all the oxygen. Then, the carbothermic reduction products were precisely mixed with an appropriate amount of carbon black to directly prepare WC-Co cemented carbides. The effects of C/WO3 ratio on the phase composition, morphological evolution, particle size and mechanical properties of products are investigated. The experimental results revealed that when the C/WO3 molar ratio was above 2.7, all oxygen in the raw material mixture were removed by carbon black and a mixture of W2C and η-phase were obtained after the first step of carbothermic reduction at 1150 °C for 2 h; then, the mixture of carbothermic reduction product and an appropriate content of carbon black was compacted, and the green compact was first carbonized at 1200 °C for 2 h and then sintered at 1450 °C for 4 h to prepare cemented carbides. With the increase of C/WO3 ratio at the first stage, the content of η-phase with a low melting point increased, which resulted in the large grain size of WC in the finally prepared cemented carbide. Compared with the traditional method of preparing cemented carbides, the cemented carbides prepared by the current method showed a higher hardness and toughness. Furthermore, the addition of a proper content of the VC in the second stage can significantly inhibit the grain growth of WC and further increase the hardness of cemented carbides.

Fabrication of spherical WC-Co powders by radio frequency inductively coupled plasma and a consequent heat treatment

Effect of processing parameters on microstructure and properties of spherical WC-Co powder by plasma spheroidization

Fabrication of spherical W–ZrC powder for additive manufacturing by spray granulation combined with plasma spheroidization

DC Arc Plasma Treatment for Defect Reduction in WC-Co Granulated Powder

Carbon control and densification of WC-8%Co fabricated by extrusion-based additive manufacturing under pressureless sintering

Fabrication and Properties of Axisymmetric WC/Co Functionally Graded Hard Metal via Microwave Sintering

Laser powder bed fusion of cemented carbides by developing a new type of Co coated WC composite powder

Preparation of WC-Co Cemented Carbide by Spark Plasma Sintering: Microstructure Evolution, Mechanical Properties and Densification Mechanism

Fabrication of WC-12Co cemented carbide by microwave sintering

Study on the RF Inductively Coupled Plasma Spheroidization of Refractory W and W-Ta Alloy Powders

Material extrusion printing of WC-8%Co cemented carbide based on partly water-soluble binder and post-processing

Phase Composition and Microstructure of Binderless Wc-Zrc Cemented Carbides Fabricated by Spark Plasma Sintering

Synthesis of Y2O3-doped WC-Co powders by wet chemical method and its effect on the properties of WC-Co cemented carbide alloy

Spark Plasma Sintering of Ultrafine WC-5%Co Cemented Carbide Composite Powders

Spark Plasma Sintering Of Nanocrystalline Wc/Co Cemented Carbides

Rapid synthesis of ultrafine WC-Co cemented carbides by in-situ reactions and spark plasma sintering

Additive manufacturing of WC-Co cemented carbides: process, microstructure, and mechanical properties

Microstructure and properties of WC-12Co cemented carbide fabricated via selective electron beam melting

In situ synthesis of spherical W Mo alloy powder for additive manufacturing by spray granulation combined with thermal plasma spheroidization

A short and facile process to synthesize WC-Co cemented carbides

Microhomogeneous WC-TiC-Co composite powders with enhanced sinterability via a two-step carburization method