Abstract:WC-Co cemented carbides are widely used in the fields of military, aerospace, mining and cutting industry etc. In this paper, a new two-step method for the preparation of WC-Co cemented carbides was proposed. First, the mixture of yellow tungsten trioxide (WO3) and cobaltic oxide (Co2O3) were reduced by carbon black to remove all the oxygen. Then, the carbothermic reduction products were precisely mixed with an appropriate amount of carbon black to directly prepare WC-Co cemented carbides. The effects of C/WO3 ratio on the phase composition, morphological evolution, particle size and mechanical properties of products are investigated. The experimental results revealed that when the C/WO3 molar ratio was above 2.7, all oxygen in the raw material mixture were removed by carbon black and a mixture of W2C and η-phase were obtained after the first step of carbothermic reduction at 1150 °C for 2 h; then, the mixture of carbothermic reduction product and an appropriate content of carbon black was compacted, and the green compact was first carbonized at 1200 °C for 2 h and then sintered at 1450 °C for 4 h to prepare cemented carbides. With the increase of C/WO3 ratio at the first stage, the content of η-phase with a low melting point increased, which resulted in the large grain size of WC in the finally prepared cemented carbide. Compared with the traditional method of preparing cemented carbides, the cemented carbides prepared by the current method showed a higher hardness and toughness. Furthermore, the addition of a proper content of the VC in the second stage can significantly inhibit the grain growth of WC and further increase the hardness of cemented carbides.

A Novel Method for Direct Synthesis of WC-Co Nanocomposite Powder

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Preparation of Ultra-Fine WC-Co Cermet and Its Wear Behavior

Study on the preparation mechanism of novel WC-Cr2(C, N)-Co nanocomposites

Preparation of nano-scaled WC powder by low-temperature carbothermic reduction method

Rapid synthesis of ultrafine WC-Co cemented carbides by in-situ reactions and spark plasma sintering

Preparation of low binder WC-Co-Ni cemented carbides with fine WC grains and homogeneous distribution of Co/Ni

Synthesis of Y2O3-doped WC-Co powders by wet chemical method and its effect on the properties of WC-Co cemented carbide alloy

Effect of Co on morphology and preparation of in situ synthesis of WC-Co composite powders

Microhomogeneous WC-TiC-Co composite powders with enhanced sinterability via a two-step carburization method

Synthesis of WC-0.67wt.%Cr3C2 nanopowders by a one-step reduction-carbonization method and their characterization

Laser powder bed fusion of cemented carbides by developing a new type of Co coated WC composite powder

A short and facile process to synthesize WC-Co cemented carbides

Low temperature pressureless immediate sintering of novel nanostructured WC/Co/NiCrSiB-alloy cemented carbide

Study on influencing factors and mechanism of high-quality tungsten carbide nanopowders synthesized via carbothermal reduction

High-performance martensitic stainless steel nanocomposite powder for direct energy deposition prepared by ball milling

A New Route For The Preparation Of Tungsten Carbide-Cobalt Nanocomposites

Preparation and characterization of high-performance in-situ synthesized WC reinforced nickel-based coatings

WC-VC/Cr3C2 composite powders prepared by a carbothermic reduction-carburization process

Fabrication of spherical WC-Co powders by radio frequency inductively coupled plasma and a consequent heat treatment

Preparation of WC-Co Cemented Carbide by Spark Plasma Sintering: Microstructure Evolution, Mechanical Properties and Densification Mechanism