Abstract:Coarse tungsten powders are usually used as raw material for preparing coarse grained WC-Co cemented carbides. Sodium can effectively promote the growth of tungsten powder during the reduction of tungsten oxide with hydrogen. Conventional addition of sodium salt into tungsten oxide powders by mechanical milling has the disadvantage of uneven distribution of sodium, which leads to abnormal growth of tungsten powders and affects the performance of WC-Co cemented carbides. In this study, uniform sodium doped ammonium paratungstate (APT) was prepared by adding sodium carbonate into ammonium tungstate solution during the evaporation and crystallization process based on the formation of ammonium-sodium paratungstate. Experimental results showed that sodium was uniformly distributed in the APT and promoted the growth of APT crystal. The sodium-doped APT was then used to produce coarse tungsten powders. Compared with tungsten powders obtained from tungsten trioxide with addition of sodium by mechanical milling, the coarse tungsten powders had larger average particle size and more uniform particle size distribution . The coarse tungsten powders were subsequently prepared into tungsten carbide powders and WC-Co cemented carbides by carburization and pressure sintering, respectively. Results showed that the obtained WC-Co cemented carbides had larger average WC grain size (6.8–7.2 μm), higher fracture toughness and transverse ruptures strength, and more uniform microstructure than that of WC-Co cemented carbides obtained by addition of sodium with mechanical milling. Moreover, sodium thoroughly volatilized during hydrogen reduction and carburization process, so that the purity of WC-Co cemented carbides was not reduced. Therefore, this study provided a new route for preparation of extra coarse-grained WC-Co cemented carbides.

A New Route For The Preparation Of Tungsten Carbide-Cobalt Nanocomposites

Long-term Ball Milling and Hot Pressing of In-Situ Nanoscale Tungsten Carbides Reinforced Copper Composite and Its Characterization

Enhanced the Mechanical Properties and Corrosion Resistance of Ultra-Coarse Grain WC-8Co Cemented Carbides by the Introduction of Cu and Ni

Preparation of Ultra-Fine WC-Co Cermet and Its Wear Behavior

Preparation Of Nanostructured W-Co Composite Powders By H-2 Plasma

A Novel Method for Direct Synthesis of WC-Co Nanocomposite Powder

Preparation Technology of Ultra-Fine Tungsten Carbide Powders: an Overview

Study on the preparation mechanism of novel WC-Cr2(C, N)-Co nanocomposites

Study on influencing factors and mechanism of high-quality tungsten carbide nanopowders synthesized via carbothermal reduction

Microhomogeneous WC-TiC-Co composite powders with enhanced sinterability via a two-step carburization method

High-gravity Combustion Synthesis and in Situ Melt Infiltration: A New Method for Preparing Cemented Carbides

Preparation of ti-al based nanophase composite powder by mechanical alloying

Preparation of extra coarse-grained WC-Co cemented carbides by doping sodium in the ammonium tungstate solution during evaporation crystallization process

A facile route to prepare ODS WC Co cemented carbides

Synthesis of Nano Tungsten Carbide Via Loose Yellow Tungsten Oxide Rod Processing

A short and facile process to synthesize WC-Co cemented carbides

Preparation of low binder WC-Co-Ni cemented carbides with fine WC grains and homogeneous distribution of Co/Ni

Preparation of nano-scaled WC powder by low-temperature carbothermic reduction method

Rapid synthesis of ultrafine WC-Co cemented carbides by in-situ reactions and spark plasma sintering

Preparation of Ti/Al based nanophase composite powder by mechanical alloying

Controllable preparation of tungsten/tungsten carbide nanowires or nanodots in nanostructured carbon with hollow macroporous core/mesoporous shell