Abstract:WC-Co cemented carbides are widely used in the fields of military, aerospace, mining and cutting industry etc. In this paper, a new two-step method for the preparation of WC-Co cemented carbides was proposed. First, the mixture of yellow tungsten trioxide (WO3) and cobaltic oxide (Co2O3) were reduced by carbon black to remove all the oxygen. Then, the carbothermic reduction products were precisely mixed with an appropriate amount of carbon black to directly prepare WC-Co cemented carbides. The effects of C/WO3 ratio on the phase composition, morphological evolution, particle size and mechanical properties of products are investigated. The experimental results revealed that when the C/WO3 molar ratio was above 2.7, all oxygen in the raw material mixture were removed by carbon black and a mixture of W2C and η-phase were obtained after the first step of carbothermic reduction at 1150 °C for 2 h; then, the mixture of carbothermic reduction product and an appropriate content of carbon black was compacted, and the green compact was first carbonized at 1200 °C for 2 h and then sintered at 1450 °C for 4 h to prepare cemented carbides. With the increase of C/WO3 ratio at the first stage, the content of η-phase with a low melting point increased, which resulted in the large grain size of WC in the finally prepared cemented carbide. Compared with the traditional method of preparing cemented carbides, the cemented carbides prepared by the current method showed a higher hardness and toughness. Furthermore, the addition of a proper content of the VC in the second stage can significantly inhibit the grain growth of WC and further increase the hardness of cemented carbides.

Synthesis of Nano Tungsten Carbide Via Loose Yellow Tungsten Oxide Rod Processing

One-dimensional Sub-stoichiometric W3O8Nanowires Filled Carbon Nanotubes

Preparation Technology of Ultra-Fine Tungsten Carbide Powders: an Overview

Study on influencing factors and mechanism of high-quality tungsten carbide nanopowders synthesized via carbothermal reduction

Preparation of nano-scaled WC powder by low-temperature carbothermic reduction method

Effect of Ball Milling Parameters on Properties of Nano-Sized Tungsten Powder via Mechanochemical Processing

Synthesis of Nanostructured Tungsten Carbide (WC) from Ammonia Paratungstate-APT and its Characterization by XRD and Rietveld Refinement

An approach for synthesizing various types of tungsten oxide nanostructure.

Controllable preparation of tungsten/tungsten carbide nanowires or nanodots in nanostructured carbon with hollow macroporous core/mesoporous shell

Fabrication of tungsten oxide powder from WC–Co cemented carbide scraps by oxidation behaviour

A short and facile process to synthesize WC-Co cemented carbides

A Novel Method for Direct Synthesis of WC-Co Nanocomposite Powder

Synthesis and Sintering of Tungsten and Titanium Carbide: A Parametric Study

A New Route For The Preparation Of Tungsten Carbide-Cobalt Nanocomposites

Synthesis of WC-0.67wt.%Cr3C2 nanopowders by a one-step reduction-carbonization method and their characterization

Research on preparation process for the in situ nanosized Zr(Y)O2 particles dispersion-strengthened tungsten alloy through synthesizing doped hexagonal (NH4)0.33·WO3

Synthesis And Characterization Of Carbide Nanorods

Sustainable and green synthesis of hydrogen tungsten bronze nanoparticles with nanocarbon via mechanically induced hydrogen spillover

Novel route to WOx nanorods and WS2 nanotubes from WS2 inorganic fullerenes.

Novel Route to WO<i><sub>x</sub></i>Nanorods and WS<sub>2</sub>Nanotubes from WS<sub>2</sub>Inorganic Fullerenes

A Simple Method for the Synthesis of Tungsten Trioxide Nanorods Array Without Catalyst