Abstract:WC-Co cemented carbides are widely used in the fields of military, aerospace, mining and cutting industry etc. In this paper, a new two-step method for the preparation of WC-Co cemented carbides was proposed. First, the mixture of yellow tungsten trioxide (WO3) and cobaltic oxide (Co2O3) were reduced by carbon black to remove all the oxygen. Then, the carbothermic reduction products were precisely mixed with an appropriate amount of carbon black to directly prepare WC-Co cemented carbides. The effects of C/WO3 ratio on the phase composition, morphological evolution, particle size and mechanical properties of products are investigated. The experimental results revealed that when the C/WO3 molar ratio was above 2.7, all oxygen in the raw material mixture were removed by carbon black and a mixture of W2C and η-phase were obtained after the first step of carbothermic reduction at 1150 °C for 2 h; then, the mixture of carbothermic reduction product and an appropriate content of carbon black was compacted, and the green compact was first carbonized at 1200 °C for 2 h and then sintered at 1450 °C for 4 h to prepare cemented carbides. With the increase of C/WO3 ratio at the first stage, the content of η-phase with a low melting point increased, which resulted in the large grain size of WC in the finally prepared cemented carbide. Compared with the traditional method of preparing cemented carbides, the cemented carbides prepared by the current method showed a higher hardness and toughness. Furthermore, the addition of a proper content of the VC in the second stage can significantly inhibit the grain growth of WC and further increase the hardness of cemented carbides.

Study on influencing factors and mechanism of high-quality tungsten carbide nanopowders synthesized via carbothermal reduction

Preparation of nano-scaled WC powder by low-temperature carbothermic reduction method

Synthesis of WC-0.67wt.%Cr3C2 nanopowders by a one-step reduction-carbonization method and their characterization

Enhanced the Mechanical Properties and Corrosion Resistance of Ultra-Coarse Grain WC-8Co Cemented Carbides by the Introduction of Cu and Ni

Tungsten carbide (WC) nanopowders synthesized via novel core–shell structured precursors

Synthesis of Tungsten Carbide Nanocrystal Via A Simple Reductive Reaction

A Novel Approach to the Rapid in Situ Synthesis of Tungsten Carbide Nanopowder by Plasma Milling and Carbothermal Reduction

Novel synthesis of hierarchical tungsten carbide micro-/nanocrystals from a single-source precursor

Study on the preparation mechanism of novel WC-Cr2(C, N)-Co nanocomposites

Preparation Technology of Ultra-Fine Tungsten Carbide Powders: an Overview

Ultrafine and Nanoscaled Tungsten Carbide Synthesis from Colloidal Carbon Coated Nano Tungsten Precursor

Preparation of Nanoscale WC Powders by Sol-Gel Synthesis and Carbon Monoxide Carbonization

A Novel Method for Direct Synthesis of WC-Co Nanocomposite Powder

Influence of Heating Rate on Formation of Nanostructured Tungsten Carbides During Thermo-Chemical Processing

Microhomogeneous WC-TiC-Co composite powders with enhanced sinterability via a two-step carburization method

Nanostructured Tungsten Carbides by Thermochemical Processing

Synthesis of nanocrystalline cubic substoichiometric WC1 − z powders by mechanochemical technology

Study on the Effect of Tungsten Content and Preheat Temperature on Combustion-Synthesized Product in Ti-W-C System

Synthesis of Nano Tungsten Carbide Via Loose Yellow Tungsten Oxide Rod Processing

Theoretical and experimental study of the mechanism for preparation of SiC nanowires by carbothermal reduction

A short and facile process to synthesize WC-Co cemented carbides