Abstract:To fulfill the demands of ceramic components with high strength, high toughness and high reliability in key projects, a novel oscillatory pressure sintering (OPS) method was proposed in this study. With this new method, zirconia ceramics with high relative density, fine grains, high fracture strength, and excellent reliability, were prepared. As a comparison, zirconia ceramics were sintered by pressure -less sintering (PS) method and hot pressing (HP) method at same temperature. SEM analysis shows that the oscillatory pressure inhibits the rapid grain growth of zirconia at high temperature. Statistic results indicate that the OPS zirconia presents fine grain size at 251 nm, while the average sizes of PS and HP zirconia are 451 and 298 nm, respectively. In addition, the oscillatory pressure induces plastic deformation of grains and sliding of grain boundaries, facilitating elimination of closed pores at grain boundaries. As a result, the relative density of OPS zirconia reaches approximately 99.7%. Due to the refinement of grains and the increase in relative density, the OPS zirconia presents an increase from 1003 MPa to 1572 MPa in flexural strength, and an increase from 13 to 32 in Weibull modulus. Furthermore, its resistance to low temperature degradation is also improved because of the microstructure evolution.

Silicon Nitride Ceramics Consolidated by Oscillatory Pressure Sintering

Optimum Sintering Temperature of High Quality Silicon Nitride Ceramics under Oscillatory Pressure

Enhanced Toughness and Reliability of Si3N4-SiCw Composites under Oscillatory Pressure Sintering

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Defects control of silicon nitride ceramics by oscillatory pressure sintering and consequent hot isotropic pressing

Microstructure and Mechanical Properties of SiC-GNPS-SiCW Ceramics by Oscillatory Pressure Sintering

Improved Mechanical Properties of Al2O3-25 Vol% SiCw Composites Prepared by Oscillatory Pressure Sintering

Enhanced Properties of Pure Alumina Ceramics by Oscillatory Pressure Sintering

Sintering behavior and mechanical properties of β-SiC ceramics under oscillatory pressure

Zirconia Ceramics Consolidated by Oscillatory Pressure Sintering and Subsequent Carburization

Microstructure and Mechanical Properties of Zirconia Ceramics Consolidated by a Novel Oscillatory Pressure Sintering

Optimization of microstructure and mechanical properties of oscillatory pressure sintered ZrO<sub>2</sub>-Al<sub>2</sub>O<sub>3</sub>-SiCp ceramics

An Oscillatory Pressure Sintering of Zirconia Powder: Densification Trajectories and Mechanical Properties

Preparation of Zirconia Ceramics with High Density and Fine Grains by Oscillatory Pressure Sintering

Sintering of High‐Performance Silicon Nitride Ceramics Under Vibratory Pressure

Optimization of microstructure and mechanical properties of oscillatory pressure sintered ZrO2–Al2O3-SiCp ceramics

Preparation of graphene nanoplatelets reinforced SiC composites by oscillatory pressure sintering

Fabrication of High-Porosity Silicon Nitride Ceramics with Excellent Mechanical Properties

Mechanical, Dielectric Properties and Thermal Shock Resistance of Porous Silicon Oxynitride Ceramics by Gas Pressure Sintering

Crack tolerant silicon carbide ceramics prepared by liquid-phase assisted oscillatory pressure sintering

Preparation of Si3n4 Ceramics with High Strength and High Reliability Via A Processing Strategy