Fabrication of Si3N4 ceramics with improved thermal conductivity by carbothermal reduction and two‐step sintering
Binbin Fan,Zunlan Hu,Shuo Zhao,Dengke Zhao,Bohan Wang,Shijia Zhang,Zhanglin Chen,Songmo Du,Fei Li,Jie Zhang,Feng Hu,Zhipeng Xie,Kexin Chen,Guanghua Liu
DOI: https://doi.org/10.1111/jace.20023
IF: 4.186
2024-07-20
Journal of the American Ceramic Society
Abstract:Si3N4 ceramics with improved thermal conductivity and mechanical properties were prepared by carbothermal reduction and two‐step sintering. The addition of 2 wt% C led to the development of an intergranular phase YNSiO2 with reduced oxygen content. Notably, setting the pre‐sintering temperature at 1450°C promoted the formation of a rough bimodal morphology within the Si3N4 ceramics. Furthermore, an extended holding period at 1850°C resulted in additional grain growth and the elimination of intergranular phases. The Si3N4 specimens produced at 1450°C for 3 h followed by 1850°C for 8 h, incorporating 2 wt% C, exhibited a notable continuity between Si3N4 grains. The thickness of the grain boundary layer was only about 1 nm, and the N/O atomic ratio of the intergranular phase was measured to be 0.42. Consequently, the resulting thermal conductivity, flexural strength, and fracture toughness of Si3N4 specimens were found to be 101 W·m−1·K−1, 712 ± 29 MPa, and 7.7 ± 0.2 MPa·m1/2, respectively. Compared with samples without C additive and directly sintered at 1850°C for 8 h, the Si3N4 specimens produced in this work showed a significant increase of more than 50% in thermal conductivity and about 17% in fracture toughness.
materials science, ceramics