Sintering of β-Si_3N_4 Powder and Thermal Conductivity of the Ceramic

Peng Mengmeng,Ning Xiaoshan

2013-01-01

Rare Metal Materials and Engineering

Abstract:Spark plasma sintering (SPS) followed by heat treatment were adopted to fabricate Si3N4 ceramics using SHS β-Si3N4 raw powder and Y2O3 -MgO additives. The sintering densification was improved by changing sintering conditions. The effect of powder type (β-Si3N4 powder or α-Si3N4 powder) and SPS holding time on thermal conductivity of the ceramics was focused. The result shows that thermal conductivity of samples fabricated with β-Si3N4 powder is above 15% higher than that of samples fabricated with α-Si3N4 powder under the same sintering conditions. Dense Si3N4 ceramics with a highest thermal conductivity of 105 W·(m·K)-1 can be prepared by spark plasma sintering at 1873K for 5 min and the followed heat treatment at 2173K for 3h.