Abstract:Silicon nitride ceramics of high thermal conductivity is a promising candidate for application as ceramic IC substrates. The thermal conductivity of Si3N4 can be changed greatly by the use of different sintering additives. In this work, different systems of additives were used to sinter the silicon nitride ceramics, including Y2O3-MgO, Y2O3-CaO, CeO2-MgO, CeO2-CaO, La2O3-MgO and La2O3-CaO, and their effects on the thermal conductivity and the mechanical and electrical properties of the sintered Si3N4 ceramics were studied. The ceramics were sintered by the spark plasma sintering (SPS) method at 1500 degrees C for 5 min which was then heat treated at 1900 degrees C for 3 h under N-2 atmosphere. Results showed that the conductivities of the ceramics sintered from the rare-earth additives tended to decrease with the increase of the cation radius in the rare-earth oxides. Different from the use of MgO, the additives of CaO did not generate the desired rod-like grains of silicon nitride which thus led to a lower thermal conductivity and a lower strength of the ceramics, although it gave a higher ceramic hardness. In contrast, the Y2O3-MgO additive system, under the optimized sintering conditions, provided a higher thermal conductivity of 80 W//m.K, with the bend strength larger than 1000 MPa. Meanwhile, the bulk resistivity was higher than 10(13)Omega.m, the dielectric constant was lower than 10 and the dielectric dissipation fraction below 3x10(-3).

Effect of Composite Sintering Additives Containing Non-Oxide on Mechanical, Thermal and Dielectric Properties of Silicon Nitride Ceramics Substrate

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Effect of Different Sintering Additives on the Reaction-Bonded Si3N4/SiC Composite Ceramics

Study on Thermal Conductivity of Si3N4 Sintered with Y2O3-MgO Additive System

Effect Of Rare-Earth Additives On Thermal Conductivity, Mechanical And Electrical Properties Of Silicon Nitride Ceramics

Study on the thermal conductivity of Si3N4 sintered with Y2O3-MgO additive system

Effect of MgF2 addition on mechanical properties and thermal conductivity of silicon nitride ceramics

Effect of Sintering Additive Composition on Microstructure and Mechanical Properties of Silicon Nitride

The influence of magnesium compounds on the properties of silicon nitride ceramics

Effects of MgSiN2 Addition and Post-Annealing on Mechanical and Thermal Properties of Si3N4 Ceramics

Comparative Study of Fluoride and Non-Fluoride Additives in High Thermal Conductive Silicon Nitride Ceramics Fabricated by Spark Plasma Sintering and Post-Sintering Heat Treatment

Study of the Thermal Conductivity of Si3N4 Sintered with CeO2 and MgO Additives

Effect of CeO2, Dy2O3, Yb 2O3 and y2O3 additives on thermal conductivity of silicon nitride ceramics

Effect of Different Sintering Additives on the Microstructure, Phase Compositions and Mechanical Properties of Si3N4/SiC Ceramics

Study on the thermal conductivity of silicon nitride ceramics with magnesia and yttria as sintering additives

Effect of Sintering Additives on Properties of Si3N4-BN Composites Fabricated Via Die Pressing and Precursor Infiltration and Pyrolysis Route

Effects of sintering additives on mechanical properties and microstructure of Si3N4 ceramics by microwave sintering

Effects of MgAl2O4-ZrO2 Addition on Sintering Behaviors and Mechanical Properties of Silicon Nitride Ceramics

Effect of Sintering Additive Composition on the Mechanical and Tribological Properties of Si3n4/Sic Ceramics

Effects of Sintering Additives on Properties of Porous Silicon Nitride Ceramics Fabricated by Carbothermal Reduction