Abstract:Si3N4 ceramics were prepared using novel two-step sintering method by mixing α-Si3N4 as raw material with nanoscale Y2O3–MgO via Y(NO3)3 and Mg(NO3)2 solutions. Si3N4 composite powders with in situ uniformly distributed Y2O3–MgO were obtained through solid–liquid (SL) mixing route. Two-step sintering method consisted of pre-deoxidization at low temperature via volatilization of in situ-formed MgSiO3 and densification at high temperature. Variations in O, Y, and Mg contents in Si3N4–Y2O3–MgO during first sintering step are discussed. O and Mg contents decreased with increasing temperature because SiO2 on Si3N4 surface reacted with MgO to form low-melting-point MgSiO3 compound, which is prone to volatilize at high temperature. By contrast, Y content hardly changed due to high-temperature stability of Y–Si–O–N quaternary compound. In the second sintering step, skeleton body was densified, and the formation of Y2Si3O3N4 secondary phase occurred simultaneously. Two-step sintered Si3N4 ceramics had lower total oxygen content (1.85 wt%) than one-step sintered Si3N4 ceramics (2.51 wt%). Therefore, flexural strength (812 MPa), thermal conductivity (92.1 W/m·K), and fracture toughness (7.6 MPa⋅m1/2) of Si3N4 ceramics prepared via two-step sintering increased by 28.7%, 16.9%, and 31.6%, respectively, compared with those of one-step sintered Si3N4 ceramics.

Silicon Nitride Ceramics with High Thermal Conductivity and Excellent Mechanical Properties Fabricated with MgF2 Sintering Aid and Post Sintering Heat Treatment

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Effects of MgSiN2 Addition and Post-Annealing on Mechanical and Thermal Properties of Si3N4 Ceramics

New Route to Improve the Fracture Toughness and Flexural Strength of Si3N4 Ceramics by Adding FeSi2

Fabrication of high thermal conductivity silicon nitride ceramics by pressureless sintering with MgO and Y2O3 as sintering additives

Effect of Post-Sintering Heat-Treatment on Thermal Conductivity of Si3N4 Ceramics Containing Different Additives

The influence of magnesium compounds on the properties of silicon nitride ceramics

Fabrication of Si3N4 ceramics with improved thermal conductivity by carbothermal reduction and two‐step sintering

Effect of Composite Sintering Additives Containing Non-Oxide on Mechanical, Thermal and Dielectric Properties of Silicon Nitride Ceramics Substrate

Sintering and Mechanical Property of Si3N4 with YF3 Sintering Aid

Fabrication of Si 3 N 4 ceramics with high thermal conductivity and flexural strength via novel two-step gas-pressure sintering

Effects of different types of sintering additives and post-heat treatment (PHT) on the mechanical properties of SHS-fabricated Si3N4 ceramics

Study on Thermal Conductivity of Si3N4 Sintered with Y2O3-MgO Additive System

Influence of α-Si3N4 coarse powder on densification, microstructure, mechanical properties, and thermal behavior of silicon nitride ceramics

Fabrication of silicon nitride with high thermal conductivity and flexural strength by hot‐pressing flowing sintering

Study on the thermal conductivity of Si3N4 sintered with Y2O3-MgO additive system

Thermal and mechanical properties of Si3N4 ceramics obtained via two-step sintering

Study on Thermal Conductivity of Spark-Plasma-Sintered Silicon Nitride Ceramics

Study on the thermal conductivity of silicon nitride ceramics with magnesia and yttria as sintering additives

An investigation on the thermal and microstructural properties of low-cost pressureless sintered silicon nitride (Si3N4) ceramics incorporated with Y2O3-SiO2-MgO

Sintering Behavior, Microstructure and Mechanical Properties of Various Fluorine-Containing Y-SiAlON Glass-Ceramics